miaobobo510新蟲 (初入文壇)
|
[求助]
麻煩給位蟲友翻譯下摘要
|
|
A sol–gel process for the preparation of thick YAG:Ce3+ films has been developed. YAG:Ce3+ phosphor films with a typical yttrium aluminum garnet (YAG) photoluminescence (PL) profile were prepared successfully. Single phase YAG films with a maximum thickness of 2 lm were prepared in the present work. The refractive index of the YAG films prepared (1.85 @ 633 nm and 1.80 @ 1540 nm) was very close to that of YAG single crystal. It was confirmed that the PL efficiency of the prepared films was strongly related to the degree of YAG phase formation in the samples and the rate of YAG phase evolution strongly depended on the film thickness. To achieve high YAG:Ce3+ PL efficiency, a minimum 1.2 lm of thickness is necessary. It was also found that the optical quality of the YAG films decreased following the deposition and thermal annealing processes, probably as a result of the growth of YAG crystals inside. As an example of a compromise between high PL efficiency and good optical quality, prism coupling was achieved on a 30-layer planar waveguide sample annealed at 1000 C for 30 min. It was proved that this sample could support multiple waveguide modes at visible wavelengths and its propagation loss at 1540 nm was estimated at 4.2 dB/cm. The temperature quenching effect in the films of the present work was also measured, being the same as that of commercial YAG:Ce3+ phosphors with relatively high Ce concentration. The present technology is intended for YAG:Ce3+ phosphor films that may be applied on white LED and it may also be of benefit to any areas where YAG films may be of interest. |
回復(fù)此樓» 猜你喜歡
303求調(diào)劑
已經(jīng)有6人回復(fù)
-
07化學(xué)303求調(diào)劑
已經(jīng)有5人回復(fù)
-
332求調(diào)劑
已經(jīng)有6人回復(fù)
-
考研調(diào)劑
已經(jīng)有7人回復(fù)
-
0856求調(diào)劑
已經(jīng)有5人回復(fù)
-
總分293求調(diào)劑
已經(jīng)有6人回復(fù)
-
275求調(diào)劑
已經(jīng)有5人回復(fù)
-
085600 材料與化工 329分求調(diào)劑
已經(jīng)有7人回復(fù)
-
材料與化工328分調(diào)劑
已經(jīng)有6人回復(fù)
-
291 求調(diào)劑
已經(jīng)有6人回復(fù)
123456zfyzfy
至尊木蟲 (知名作家)
- 應(yīng)助: 0 (幼兒園)
- 金幣: 28394.2
- 紅花: 75
- 帖子: 5232
- 在線: 465.7小時(shí)
- 蟲號(hào): 2411699
- 注冊(cè): 2013-04-10
- 專業(yè): 合成藥物化學(xué)
2樓2014-01-01 18:13:40
miaobobo510
新蟲 (初入文壇)
- 應(yīng)助: 0 (幼兒園)
- 金幣: 596.5
- 帖子: 38
- 在線: 7.8小時(shí)
- 蟲號(hào): 2780079
- 注冊(cè): 2013-11-05
- 專業(yè): 資源化工
3樓2014-01-02 10:24:08
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 miaobobo510 的主題更新
| 3 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 0856求調(diào)劑 +4 | zhn03 2026-03-25 | 5/250 |
|
|---|---|---|---|---|
|
|
[考研] 總分293求調(diào)劑 +4 | 加一一九 2026-03-25 | 6/300 |
|
|
|
[考研] 291 求調(diào)劑 +5 | 化工2026屆畢業(yè)?/a> 2026-03-21 | 6/300 |
|
|
|
[考研] 08工學(xué)調(diào)劑 +13 | 用戶573181 2026-03-20 | 18/900 |
|
|
[考研] 北科281學(xué)碩材料求調(diào)劑 +13 | tcxiaoxx 2026-03-20 | 15/750 |
|
|
|
[考研] 一志愿中南大學(xué)化學(xué)學(xué)碩0703總分337求調(diào)劑 +7 | niko- 2026-03-22 | 7/350 |
|
|
|
[考研] 機(jī)械學(xué)碩總分317求調(diào)劑！�。�！ +4 | Acaciad 2026-03-25 | 4/200 |
|
|
|
[考研] 296求調(diào)劑 +4 | 汪�。�！ 2026-03-25 | 7/350 |
|
|
|
[考研] 359求調(diào)劑 +3 | 王了個(gè)楠 2026-03-25 | 3/150 |
|
|
|
[考研] 287求調(diào)劑 +10 | 晨昏線與星海 2026-03-19 | 11/550 |
|
|
|
[考研] 材料專碩331求調(diào)劑 +4 | 鮮當(dāng)牛 2026-03-24 | 4/200 |
|
|
|
[考研] 一志愿河北工業(yè)大學(xué)0817化工278分求調(diào)劑 +7 | jhybd 2026-03-23 | 12/600 |
|
|
|
[基金申請(qǐng)] 請(qǐng)教下大家 2026年國(guó)家基金申請(qǐng)是雙盲審嗎？ +3 | lishucheng1 2026-03-22 | 5/250 |
|
|
|
[考研] 化學(xué)308分求調(diào)劑 +3 | 你好明天你好 2026-03-23 | 3/150 |
|
|
|
[考研] 275求調(diào)劑 +6 | shansx 2026-03-22 | 8/400 |
|
|
|
[考研] 求調(diào)劑 +7 | Auroracx 2026-03-22 | 7/350 |
|
|
|
[考研] 求調(diào)劑 +4 | 要好好無聊 2026-03-21 | 4/200 |
|
|
|
[考研] 一志愿蘇州大學(xué)材料求調(diào)劑，總分315（英一） +5 | sbdksD 2026-03-19 | 5/250 |
|
|
|
[考研] 一志愿西安交通大學(xué) 學(xué)碩 354求調(diào)劑211或者雙一流 +3 | 我想要讀研究生 2026-03-20 | 3/150 |
|
|
|
[考研] 材料學(xué)碩318求調(diào)劑 +5 | February_Feb 2026-03-19 | 5/250 |
|