塑料薄膜的拉伸模量測量
|
|
In this study the tensile stress/strain behavior of various consumer plastic thin film materials was measured using a low mass mechanical analyzer. Film thicknesses varied from 19 mm to 66 mm (0.75 mil to 2.6 mil). In this study the force applied to the samples was ramped at 0.05 N/min from 0.05 N to 1 N and sample strain was followed. All measurements were made at ambient conditions. The tensile behavior of the consumer products were compared qualitatively and quantitatively. Three mechanical phenomena were observed in the materials: linear elastic behavior, a strengthening or increase in modulus, and yielding or rapid elongation with minimal changes in stress. In the linear elastic region modulus was measured as defined by the inverse of the slope of the stress versus strain curve. Modulus values of 87 MPa to 6 GPa were observed. |
回復(fù)此樓» 本帖附件資源列表
-
歡迎監(jiān)督和反饋：小木蟲僅提供交流平臺，不對該內(nèi)容負(fù)責(zé)。
本內(nèi)容由用戶自主發(fā)布，如果其內(nèi)容涉及到知識產(chǎn)權(quán)問題，其責(zé)任在于用戶本人，如對版權(quán)有異議，請聯(lián)系郵箱：xiaomuchong@tal.com - 附件 1 : 塑料薄膜的拉伸模量.PDF
2016-03-30 09:11:41, 791.07 K
» 猜你喜歡
求材料調(diào)劑
已經(jīng)有8人回復(fù)
-
294求調(diào)劑材料與化工專碩
已經(jīng)有5人回復(fù)
-
一志愿華中科技大學(xué)，080502，354分求調(diào)劑
已經(jīng)有4人回復(fù)
-
一志愿吉林大學(xué)材料學(xué)碩321求調(diào)劑
已經(jīng)有6人回復(fù)
-
085410人工智能專碩317求調(diào)劑（0854都可以）
已經(jīng)有3人回復(fù)
-
330求調(diào)劑
已經(jīng)有3人回復(fù)
-
一志愿中海洋材料工程專碩330分求調(diào)劑
已經(jīng)有5人回復(fù)
-
304求調(diào)劑
已經(jīng)有5人回復(fù)
-
311求調(diào)劑
已經(jīng)有4人回復(fù)
-
354求調(diào)劑
已經(jīng)有7人回復(fù)
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 TAINST 的主題更新
| 1 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 330求調(diào)劑 +3 | 小材化本科 2026-03-18 | 3/150 |
|
|---|---|---|---|---|
|
|
[考研] 321求調(diào)劑 +3 | 何潤采123 2026-03-18 | 3/150 |
|
|
[考研] 能源材料化學(xué)課題組招收碩士研究生8-10名 +4 | 脫穎而出 2026-03-16 | 10/500 |
|
|
|
[考研] 302求調(diào)劑 +10 | 呼呼呼。。。。 2026-03-17 | 10/500 |
|
|
|
[考研] 307求調(diào)劑 +3 | 冷笙123 2026-03-17 | 3/150 |
|
|
|
[基金申請] 被我言中：新模板不強調(diào)格式了，假專家開始管格式了 +4 | beefly 2026-03-14 | 4/200 |
|
|
|
[考研] 考研求調(diào)劑 +3 | 橘頌. 2026-03-17 | 4/200 |
|
|
|
[考研] 材料工程專碩調(diào)劑 +5 | 204818@lcx 2026-03-17 | 5/250 |
|
|
|
[考研] 【0856】化學(xué)工程（085602）313 分，本科學(xué)科評估A類院�；瘜W(xué)工程與工藝，誠求調(diào)劑 +7 | 小劉快快上岸 2026-03-11 | 8/400 |
|
|
|
[考研] 26考研求調(diào)劑 +6 | 丶宏Sir 2026-03-13 | 6/300 |
|
|
|
[考研] 有沒有道鐵/土木的想調(diào)劑南林，給自己招師弟中～ +3 | TqlXswl 2026-03-16 | 7/350 |
|
|
|
[考研] 211本，11408一志愿中科院277分，曾在中科院自動化所實習(xí) +6 | Losir 2026-03-12 | 7/350 |
|
|
|
[考研] 275求調(diào)劑 +4 | 太陽花天天開心 2026-03-16 | 4/200 |
|
|
|
[考研] 0703一志愿211 285分求調(diào)劑 +5 | ly3471z 2026-03-13 | 5/250 |
|
|
|
[考研] 0703 物理化學(xué)調(diào)劑 +3 | 我可以上岸的對?/a> 2026-03-13 | 5/250 |
|
|
|
[考博] 東華理工大學(xué)化材專業(yè)26屆碩士博士申請 +6 | zlingli 2026-03-13 | 6/300 |
|
|
|
[考研] 0856專碩279求調(diào)劑 +5 | 加油加油！? 2026-03-15 | 5/250 |
|
|
|
[考研] 265求調(diào)劑 +4 | 威化餅07 2026-03-12 | 4/200 |
|
|
|
[考研] 招收0805（材料）調(diào)劑 +3 | 18595523086 2026-03-13 | 3/150 |
|
|
|
[考研] 274求調(diào)劑 +3 | S.H1 2026-03-12 | 3/150 |
|