Capping agent exchange with PVP 請問各位大神這個是什么意思?
|
|
Capping agent exchange with PVP The obtained Co2P nanoparticles were dissolved in 10 mL n-hexane and added to a solution containing 200 mL trichloromethane and 2.0 g PVP. The reaction was then heated to 65 ℃ and refluxed for 12 h under an Ar atmosphere. After the mixture was cooled to room temperature, acetone was added to cause flocculation and the mixture was centrifuged to separate the black precipitate. The obtained black solid was washed with acetone three times and dried in a vacuum oven. The final product could readily dissolve in water. 為什么磷化鈷經(jīng)過這些步驟處理后就能夠溶于水呢?各位知道的麻煩解答一下啊,感激不盡! |

鐵蟲 (初入文壇)
|
Co2P被PVP包覆后在水里面分散性就好了吧 發(fā)自小木蟲Android客戶端 |

金蟲 (正式寫手)
|
原來它既表面穩(wěn)定劑是什么? 發(fā)自小木蟲Android客戶端 |

金蟲 (著名寫手)

金蟲 (著名寫手)

銀蟲 (正式寫手)
|
用PVP進(jìn)行保護(hù)劑交換,就是用PVP取代原保護(hù)劑 發(fā)自小木蟲IOS客戶端 |
金蟲 (著名寫手)

銀蟲 (正式寫手)
金蟲 (著名寫手)
送紅花一朵 |
文獻(xiàn)中它是用來做助催化劑負(fù)載到硫化鎘納米棒上。文獻(xiàn)的意思是將磷化鈷和硫化鎘納米棒分別制備出來,然后將制備的磷化鈷經(jīng)過上述步驟處理后和硫化鎘納米棒一起溶于水中,然后磷化鈷就能夠被硫化鎘納米棒吸附在上面,照您的意思是不是PVP作為磷化鈷的保護(hù)劑將磷化鈷包裹起來,由于PVP溶于水,所以也讓磷化鈷溶于水,能夠更好的分散在水中被硫化鎘納米棒吸附? 還有,我想請問一下加熱回流的目的是不是為了讓PVP和磷化鈷更好更充份的接觸從而讓磷化鈷被PVP包裹起來,那么如果不回流行不行。 還有我覺得沒必要通氬氣吧,也沒有什么容易被氧化的物質(zhì),而且既加熱回流又要通氬氣,那么這個裝置就太復(fù)雜了。 |

銀蟲 (正式寫手)
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 281求調(diào)劑 +4 | Koxui 2026-03-24 | 5/250 |
|
|---|---|---|---|---|
|
[考研] 上海電力大學(xué)材料防護(hù)與新材料重點(diǎn)實(shí)驗(yàn)室招收調(diào)劑研究生(材料、化學(xué)、電化學(xué),環(huán)境) +4 | 我愛學(xué)電池 2026-03-23 | 4/200 |
|
|
[考研] 0854AI CV方向招收調(diào)劑 +3 | 章小魚567 2026-03-23 | 3/150 |
|
|
[考研] 070300化學(xué)求調(diào)劑 +9 | 苑豆豆 2026-03-20 | 9/450 |
|
|
[考研]
|
黃粱一夢千年 2026-03-24 | 3/150 |
|
|
[考研] 291求調(diào)劑 +3 | HanBeiNingZC 2026-03-24 | 3/150 |
|
|
[考研] 一志愿北京化工大學(xué)材料與化工 264分各科過A區(qū)國家線 +3 | 哈哈157349 2026-03-21 | 3/150 |
|
|
[考研] 一志愿哈工大,085400,320,求調(diào)劑 +3 | gdlf9999 2026-03-24 | 3/150 |
|
|
[考研] 327求調(diào)劑 +5 | prayer13 2026-03-23 | 5/250 |
|
|
[考研]
求調(diào)劑材料學(xué)碩080500,總分289分
5+3
|
@taotao 2026-03-19 | 21/1050 |
|
|
[考研] 306求調(diào)劑 +5 | 來好運(yùn)來來來 2026-03-22 | 5/250 |
|
|
[考研] 298求調(diào)劑一志愿211 +3 | 上岸6666@ 2026-03-20 | 3/150 |
|
|
[考研] 311求調(diào)劑 +3 | 26研0 2026-03-20 | 3/150 |
|
|
[考研] 一志愿北京化工大學(xué)070300 學(xué)碩336求調(diào)劑 +5 | vv迷 2026-03-21 | 8/400 |
|
|
[考研] 求調(diào)劑 +3 | 13341 2026-03-20 | 3/150 |
|
|
[考研] 材料學(xué)碩333求調(diào)劑 +3 | 北道巷 2026-03-18 | 3/150 |
|
|
[考研] 265求調(diào)劑 +12 | 梁梁校校 2026-03-19 | 14/700 |
|
|
[考研] 一志愿武漢理工材料工程專碩調(diào)劑 +9 | Doleres 2026-03-19 | 9/450 |
|
|
[考研] 一志愿 西北大學(xué) ,070300化學(xué)學(xué)碩,總分287,雙非一本,求調(diào)劑。 +4 | 晨昏線與星海 2026-03-19 | 4/200 |
|
|
[考研] 261求B區(qū)調(diào)劑,科研經(jīng)歷豐富 +3 | 牛奶很忙 2026-03-20 | 4/200 |
|