[求助]
合成檸檬酸根修飾的磁性納米粒子時遇到的問題
|
|||
|
文獻(xiàn)上的制備方法： Magnetite(Fe3O4) particles were prepared by co-precipitation of FeCl2 and FeCl3 (1:2 molar ratio) by the addition of NH4OH. In a typical reaction, 0.86 g FeCl2 and 2.35 g FeCl3 were mixed in 40 ml water and heated to 80º C under argon in a three-necked flask. While vigorously stirring the reaction mixture, 5 ml of NH4OH was introduced by syringe and the heating continued for thirty minutes. After that, 1g of citric acid (CA) in 2ml water was introduced, the temperature raised to 95º C and the stirring continued for an additional ninety minutes. A small aliquot of the reaction mixture was withdrawn, diluted to twice its volume and placed on a 0.5 Tesla magnet in a vial. At the point when the particles did not settle down under the influence of the magnet, the colloidal solution was stable. The as-formed reaction product contained an excess of citric acid. Therefore, the nanoparticle dispersion was subjected to dialysis against water in a 12-14 kD cut-off cellulose membrane (Spectrum Laboratories, Inc., USA) for 72 hours to remove the excess unbound CA. The citric acid coated magnetic particles are abbreviated as MP-CA. 我的疑問： 反應(yīng)在較高溫度下進(jìn)行了很長時間(至少2小時)，體系一直在通氬氣，為了保證內(nèi)部氣壓不至于過高，肯定要有出氣孔，這這么高溫度和這么長時間下，體系的水幾乎都揮發(fā)沒了，請問這個問題如何處理？ 謝謝，盼指導(dǎo)！ |
回復(fù)此樓» 猜你喜歡
北京航空航天大學(xué)26級博士招生-生物醫(yī)學(xué)工程-合成生物學(xué)
已經(jīng)有20人回復(fù)
-
溫州大學(xué)王娟課題組2026年招生
已經(jīng)有10人回復(fù)
-
金屬材料論文潤色/翻譯怎么收費(fèi)?
已經(jīng)有189人回復(fù)
-
溫州大學(xué)2026年招生（化學(xué)、材料）
已經(jīng)有10人回復(fù)
-
招生負(fù)責(zé)_院士團(tuán)隊_學(xué)生高自由度成長_擅長學(xué)生培養(yǎng)
已經(jīng)有5人回復(fù)
-
溫州大學(xué)招收2026年入學(xué)博士研究生（化學(xué)、材料、環(huán)境）
已經(jīng)有10人回復(fù)
-
非晶合金
已經(jīng)有2人回復(fù)
-
院士團(tuán)隊-每屆學(xué)生都優(yōu)秀-高自由度-團(tuán)隊氛圍好
已經(jīng)有0人回復(fù)
-
求調(diào)劑
已經(jīng)有1人回復(fù)
-
化工學(xué)院（學(xué)院正式調(diào)劑群+聯(lián)系方式）
已經(jīng)有0人回復(fù)
» 本主題相關(guān)商家推薦: (我也要在這里推廣)
» 本主題相關(guān)價值貼推薦，對您同樣有幫助:
- 金納米粒子修飾后溶液中出現(xiàn)絮狀物
已經(jīng)有9人回復(fù)
- 我用共沉淀法合成四氧化三鐵磁性納米，合成好之后加入檸檬酸還是會聚沉呢？
已經(jīng)有24人回復(fù)
- 為什么合成出來的鎳納米粒子沒有磁性
已經(jīng)有13人回復(fù)
- 【討論】關(guān)于金納米粒子合成的問題
已經(jīng)有46人回復(fù)
- 【討論】檸檬酸根包被的金納米粒子 這句話怎么理解？
已經(jīng)有9人回復(fù)
- 【求助】金銀合金納米粒子合成遇到的問題
已經(jīng)有15人回復(fù)
- 【求助】納米金表面修飾---檸檬酸根和CTAB
已經(jīng)有22人回復(fù)
- 【請教】磁性納米材料Fe3O4/Al2O3的合成中的問題
已經(jīng)有24人回復(fù)
refnew
專家顧問 (知名作家)
-
專家經(jīng)驗: +181 - MN-EPI: 4
- 應(yīng)助: 678 (博士)
- 貴賓: 0.577
- 金幣: 9465.7
- 散金: 229
- 紅花: 54
- 帖子: 6391
- 在線: 1613.5小時
- 蟲號: 33447
- 注冊: 2003-12-31
- 性別: GG
- 專業(yè): 納米生物學(xué)
- 管轄: 微米和納米
4樓2012-05-05 10:46:12
refnew
專家顧問 (知名作家)
-
專家經(jīng)驗: +181 - MN-EPI: 4
- 應(yīng)助: 678 (博士)
- 貴賓: 0.577
- 金幣: 9465.7
- 散金: 229
- 紅花: 54
- 帖子: 6391
- 在線: 1613.5小時
- 蟲號: 33447
- 注冊: 2003-12-31
- 性別: GG
- 專業(yè): 納米生物學(xué)
- 管轄: 微米和納米
2樓2012-05-05 10:13:33
3樓2012-05-05 10:22:48
5樓2012-05-05 10:47:34
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 一志愿天津大學(xué)化學(xué)工藝專業(yè)（081702）315分求調(diào)劑 +10 | yangfz 2026-03-17 | 10/500 |
|
|---|---|---|---|---|
|
[考研] 一志愿中海洋材料工程專碩330分求調(diào)劑 +4 | 小材化本科 2026-03-18 | 4/200 |
|
|
|
[考研] 0703化學(xué)調(diào)劑，求各位老師收留 +9 | 秋有木北 2026-03-14 | 9/450 |
|
|
|
[考研] 0703化學(xué) 305求調(diào)劑 +3 | FY_yy 2026-03-14 | 3/150 |
|
|
|
[考研] 一志愿西南交大，求調(diào)劑 +4 | 材化逐夢人 2026-03-18 | 4/200 |
|
|
|
[考研] 生物學(xué)071000 329分求調(diào)劑 +3 | 我愛生物生物愛?/a> 2026-03-17 | 3/150 |
|
|
|
[考研] 0703化學(xué)336分求調(diào)劑 +6 | zbzihdhd 2026-03-15 | 7/350 |
|
|
|
[考研] 268求調(diào)劑 +7 | 好運(yùn)連綿不絕 2026-03-12 | 8/400 |
|
|
|
[考研] 考研調(diào)劑 +3 | 淇ya_~ 2026-03-17 | 5/250 |
|
|
|
[考研] 278求調(diào)劑 +3 | Yy7400 2026-03-13 | 3/150 |
|
|
|
[考研] 東南大學(xué)364求調(diào)劑 +5 | JasonYuiui 2026-03-15 | 5/250 |
|
|
|
[考研] 藥學(xué)383 求調(diào)劑 +3 | 藥學(xué)chy 2026-03-15 | 4/200 |
|
|
|
[考研] 333求調(diào)劑 +3 | 文思客 2026-03-16 | 7/350 |
|
|
|
[考研] 304求調(diào)劑 +4 | ahbd 2026-03-14 | 4/200 |
|
|
|
[考研] 318求調(diào)劑 +3 | Yanyali 2026-03-15 | 3/150 |
|
|
|
[考研]
 機(jī)械專碩調(diào)劑
+3
|
笨笨兔子 2026-03-12 | 3/150 |
|
|
|
[考研] 0856專碩279求調(diào)劑 +5 | 加油加油！? 2026-03-15 | 5/250 |
|
|
|
[考研] 080500，材料學(xué)碩302分求調(diào)劑學(xué)校 +4 | 初識可樂 2026-03-14 | 5/250 |
|
|
|
[考研] 一志愿哈工大材料324分求調(diào)劑 +5 | 閆旭東 2026-03-14 | 5/250 |
|
|
|
[考研] 277求調(diào)劑 +4 | anchor17 2026-03-12 | 4/200 |
|