oink銀蟲 (著名寫手)
|
[求助]
跪求翻譯
|
||
|
3. Results and discussion 3.1. FTIR analysis FTIR spectra are commonly employed to identify the change of characteristic groups. Fig. 1 presented the FTIR spectra of PAL samples. It could be seen that the absorption bands at 1030 and 983 cm−1 were ascribed to the Si\O stretching vibrations [22], and the absorption bands at 519 and 478 cm−1 were attributed to the Si\O bending vibrations. The bands at 3411 and 1646 cm−1 were assigned to the characteristic O\H stretching and H\O\H bending vibration of the coordinated and adsorbed water in PAL samples, respectively. The broad bands at 3621–3543 cm−1 were ascribed to the stretching vibrations of (Al)O\H and (Mg)O\H bonds. As could be seen from Fig. 1, compared with the spectrum of PAL-0, for PAL-6, the absorption bands (1030 and 983 cm−1) became blunt and the strength reduced. And there were no other obvious differences among the characteristic absorption bands of PAL samples.3.2. FESEM analysis The FESEM micrographs of PAL-0, PAL-4, PAL-6 and PAL-8 were observed and shown in Fig. 2. It can be seen from Fig. 2a, the rodlike crystals of PAL were well developed with a length up to 1 μm and a diameter of about 50–80 nm. The rod-like crystals of PAL were tightly packed due to the actions of van der Waals force and hydrogen bonds. After grinding treatment (PAL-4 and PAL-6), some rod-like crystals of PAL became shorter (Fig. 2b and c), the crystal bundles were partially dissociated and the dispersion degree of PAL crystals was improved. However, the rod-like crystals obviously got shorter when the grinding times were further increased (PAL-8), and most of them were in the form of granules (Fig. 2d). The crystal aggregates were significantly dissociated and the structure of PAL-8 was modified. The results could be explained as follows. The interaction among the rod–like single crystals of PAL is weak because of a line–line like contact [23]. When raw PAL was grinded, the two disks of stone miller generated strong compression, shearing stress and looping stress, which split the crystal bundles into individual rodlike crystals and the crystal aggregates were dissociated. With increasing the grinding times, the continual shearing stress and looping stress acting on the rod-like crystals of PAL increased, and induced the breakage of rod-like crystals, and therefore the crystal rods will be shorter. That is to say, large shearing forces resulting from the stone miller operating on the PAL can make the crystal aggregates and bundles into several crystal bundles or single crystals. However, if the strong shearing stress continues for a long time, it can cause serious damage to the long single crystals of PAL before obtaining high dispersion. In this case, to search out appropriate grinding times is essential and it can be said that the method of grinding treatment on PAL with appropriate grinding times can disperse part of the crystal aggregates into small crystal bundles and rod-like single crystals, which is helpful to extend the practical application of PAL. 3.3. XRD analysis X-ray diffraction patterns of PAL samples were presented in Fig. 3. A characteristic reflection peak of PAL at 2θ=8.38º (d=10.6 Å  [24]can be observed for all the PAL samples with greater intensity, indicating the order–disorder structural degree of PAL was very high. The appearance of the diffraction peak at 2θ=26.5º (d=3.36 Å and 2θ=31.0º (d=2.88 Å revealed that PAL contains minor contents(contaminants) of quartz and dolomite [24,25]. As the grinding times increased to 4, no significant change in diffraction peaks can be observed between the X-ray patterns of PAL-0, PAL-2 and PAL-4, suggesting the crystal structure of PAL was not affected in the processesystals, which is helpful to extend the practical application of PAL. |
回復(fù)此樓» 猜你喜歡
309求調(diào)劑
已經(jīng)有8人回復(fù)
-
一志愿南航 335分 | 0856 | GPA 4.07 | 有科研經(jīng)歷
已經(jīng)有8人回復(fù)
-
求調(diào)劑
已經(jīng)有5人回復(fù)
-
求化學(xué)調(diào)劑
已經(jīng)有5人回復(fù)
-
085600，材料與化工321分求調(diào)劑
已經(jīng)有10人回復(fù)
-
0703 化學(xué) 求調(diào)劑，一志愿山東大學(xué) 342 分
已經(jīng)有5人回復(fù)
-
一志愿南開大學(xué)0710生物學(xué)359求調(diào)劑
已經(jīng)有3人回復(fù)
-
085600，專業(yè)課化工原理，320分求調(diào)劑
已經(jīng)有4人回復(fù)
-
材料與化工272求調(diào)劑
已經(jīng)有16人回復(fù)
-
290求調(diào)劑
已經(jīng)有3人回復(fù)
phu_grassman
榮譽(yù)版主 (知名作家)
快樂(lè)島、布吉島島主
- 翻譯EPI: 265
- 應(yīng)助: 7 (幼兒園)
- 貴賓: 1.392
- 金幣: 7538.7
- 散金: 11599
- 紅花: 107
- 沙發(fā): 11
- 帖子: 5611
- 在線: 1480.2小時(shí)
- 蟲號(hào): 1151372
- 注冊(cè): 2010-11-20
- 專業(yè): 電化學(xué)
- 管轄: English Cafe
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
愛(ài)與雨下: 金幣+2 2012-10-22 19:55:21
oink: 金幣+25, 翻譯EPI+1, ★★★很有幫助, 謝謝了 2012-10-24 10:50:05
愛(ài)與雨下: 金幣+2 2012-10-22 19:55:21
oink: 金幣+25, 翻譯EPI+1, ★★★很有幫助, 謝謝了 2012-10-24 10:50:05
|
3.1 傅里葉紅外光譜（FTIR）分析 紅外光譜通常被用來(lái)鑒別特征基團(tuán)的變化。圖1為PAL樣品的紅外光譜�？梢钥闯�1030和983cm-1出的吸收譜帶歸屬于Si\O的伸縮振動(dòng)，519和478處的吸收峰被歸屬為Si\O的彎曲振動(dòng)。3411和1646處峰分別是PAL樣品中配合水和吸收水中O/H伸縮振動(dòng)及H/O/H彎曲振動(dòng)。3621-3543處的寬峰歸屬為 (Al)O\H 和(Mg)O\H鍵的伸縮振動(dòng)。從圖1可以看出，與PAL-0的譜圖相比，PAL-6在1030和983處的吸收峰變寬且強(qiáng)度降低。此外PAL樣品的特征吸收峰之間并無(wú)明顯差異。 太多了，自個(gè)慢慢翻譯吧。  |
3樓2012-10-22 19:23:06
ywithm
金蟲 (小有名氣)
- 應(yīng)助: 2 (幼兒園)
- 金幣: 1355.2
- 帖子: 83
- 在線: 39.8小時(shí)
- 蟲號(hào): 1669466
- 注冊(cè): 2012-03-06
- 性別: GG
- 專業(yè): 金屬有機(jī)化學(xué)
2樓2012-10-22 16:22:11
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 307求調(diào)劑 +9 | 超級(jí)伊昂大王 2026-03-24 | 10/500 |
|
|---|---|---|---|---|
|
[考研] 318一志愿吉林大學(xué)生物與醫(yī)藥 求調(diào)劑 +4 | 篤行致遠(yuǎn). 2026-03-28 | 4/200 |
|
|
|
[考研] 356求調(diào)劑 +4 | gysy?s?a 2026-03-28 | 4/200 |
|
|
|
[考研] 0856材料化工調(diào)劑 總分330 +14 | zhubinhao 2026-03-27 | 14/700 |
|
|
|
[考研] 330分求調(diào)劑 +5 | qzenlc 2026-03-29 | 5/250 |
|
|
|
[考研] 0703化學(xué)調(diào)劑，求導(dǎo)師收 +9 | 天天好運(yùn)來(lái)上岸?/a> 2026-03-24 | 10/500 |
|
|
|
[考研] 一志愿太原理工安全工程300分，求調(diào)劑 +5 | 0857求調(diào)劑. 2026-03-24 | 6/300 |
|
|
|
[考研] 332求調(diào)劑 +4 | @MZB382400 2026-03-28 | 4/200 |
|
|
|
[考研] 復(fù)試調(diào)劑 +3 | raojunqi0129 2026-03-28 | 3/150 |
|
|
|
[考研] 291求調(diào)劑 +15 | hhhhxn.. 2026-03-23 | 21/1050 |
|
|
|
[考研] 0703化學(xué)求調(diào)劑，各位老師看看我�。�！ +5 | 祁祺祺 2026-03-25 | 5/250 |
|
|
|
[考研] 285求調(diào)劑 +4 | AZMK 2026-03-27 | 7/350 |
|
|
|
[考研] 085600，材料與化工321分，求調(diào)劑 +9 | 大饞小子 2026-03-27 | 9/450 |
|
|
|
[考研] 0703化學(xué)338求調(diào)劑！ +6 | Zuhui0306 2026-03-26 | 7/350 |
|
|
|
[考研] 276求調(diào)劑。有半年電池和半年高分子實(shí)習(xí)經(jīng)歷 +10 | 材料學(xué)257求調(diào)劑 2026-03-23 | 11/550 |
|
|
|
[考研] 求調(diào)劑，一志愿 南京航空航天大學(xué)大學(xué) ，080500材料科學(xué)與工程學(xué)碩 +4 | @taotao 2026-03-26 | 5/250 |
|
|
|
[考研] 打過(guò)很多競(jìng)賽，085406控制工程300分，求調(diào)劑 +3 | askeladz 2026-03-26 | 3/150 |
|
|
|
[考研] 材料專碩 335 分求調(diào)劑 +4 | 拒絕冷暴力 2026-03-25 | 4/200 |
|
|
|
[考研] 086003食品工程求調(diào)劑 +6 | 淼淼111 2026-03-24 | 6/300 |
|
|
|
[考研] 335求調(diào)劑 +4 | yuyu宇 2026-03-23 | 5/250 |
|