lofed銅蟲 (小有名氣)
|
[求助]
求大神翻譯哈，重謝！
|
|
| Reagents were all of AR grade. Water used in the synthesis and washing was deionized. Graphite oxide was prepared from natural graphite powder by a modification of Hummers method.[17] One gram of graphite powder was added to 23 mL of cooled (0°C) concentrated H2SO4。Three temperature of the mixture was maintained below 20°C. The mixture was then stirred at 35°C for 30 min. 46 mL of distilled water was slowly added to cause an increase in temperature to 98°C, and the mixture was maintained at that temperature for 15 min. The reaction was terminated by adding 140 mL of distilled water followed by 10 mL of 30% H2O2 solution. The solid product was separated by centrifugation, washed repeatedly with 5% HCl solution until sulfate could not be detected with BaCl2, and then washed 3-4 times with ethanol and dried in vacuum at 60°C overnight. |
回復此樓» 猜你喜歡
南京大學化學調(diào)劑
已經(jīng)有14人回復
-
一志愿北京工業(yè)大學，324分求調(diào)劑
已經(jīng)有6人回復
-
一志愿河北工業(yè)大學0817化工278分求調(diào)劑
已經(jīng)有14人回復
-
求調(diào)劑
已經(jīng)有5人回復
-
281求調(diào)劑
已經(jīng)有6人回復
-
26申博自薦
已經(jīng)有6人回復
-
一志愿哈爾濱工業(yè)大學材料與化工方向336分
已經(jīng)有10人回復
-
求調(diào)劑 有機化學考研356分
已經(jīng)有5人回復
-
300求調(diào)劑，材料科學英一數(shù)二
已經(jīng)有10人回復
-
材料與化工328分調(diào)劑
已經(jīng)有7人回復
lofed
銅蟲 (小有名氣)
- 應(yīng)助: 0 (幼兒園)
- 金幣: 263.6
- 帖子: 91
- 在線: 48.4小時
- 蟲號: 1479766
- 注冊: 2011-11-07
- 性別: GG
- 專業(yè): 有機合成
送紅花一朵 
3樓2013-12-27 11:30:25
phu_grassman
榮譽版主 (知名作家)
快樂島、布吉島島主
- 翻譯EPI: 265
- 應(yīng)助: 7 (幼兒園)
- 貴賓: 1.392
- 金幣: 7538.7
- 散金: 11599
- 紅花: 107
- 沙發(fā): 11
- 帖子: 5611
- 在線: 1480.2小時
- 蟲號: 1151372
- 注冊: 2010-11-20
- 專業(yè): 電化學
- 管轄: English Cafe
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★
lofed: 金幣+10, 翻譯EPI+1, ★★★★★最佳答案, 非常感謝！ 2013-12-27 11:28:47
lofed: 金幣+10, 翻譯EPI+1, ★★★★★最佳答案, 非常感謝！ 2013-12-27 11:28:47
| 實驗中所有的試劑均是分析純。合成和洗滌過程中所用的為去離子水。氧化石墨烯由天然石墨粉末通過改進的Hummer法制得。1 g石墨粉末加入到23 mL冷卻的濃硫酸中。（Three temperature of the mixture was maintained below 20°C. 這句沒看明白，three是不是the？）混合物的溫度保持在20度以下，然后在35度下攪拌30 min，之后緩慢加入46 mL蒸餾水使混合物溫度增加到98度，并保持在此溫度15 min。最后通過先后加入14o mL蒸餾水、1o mL30% 的雙氧水溶液使反應(yīng)終止。固體產(chǎn)品通過離心分離，并用5%HCl溶液反復洗滌，直至硫酸根粒子不能通過BaCl2被檢測到。然后用乙醇洗滌3-4遍，并于60度下過夜真空干燥。 |
» 本帖已獲得的紅花（最新10朵）
2樓2013-12-26 23:45:43
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 一志愿北京化工大學材料與化工（085600）296求調(diào)劑 +17 | 稻妻小編 2026-03-26 | 17/850 |
|
|---|---|---|---|---|
|
[考研] 環(huán)境工程 085701，267求調(diào)劑 +6 | minht 2026-03-29 | 6/300 |
|
|
|
[考研] 085600，專業(yè)課化工原理，321分求調(diào)劑 +5 | 大饞小子 2026-03-28 | 5/250 |
|
|
|
[考研] 298求調(diào)劑 +4 | 種圣賜 2026-03-28 | 4/200 |
|
|
|
[考研] 289求調(diào)劑 +13 | 新時代材料 2026-03-27 | 13/650 |
|
|
|
[考研] 295材料工程專碩求調(diào)劑 +7 | 1428151015 2026-03-27 | 7/350 |
|
|
|
[考研] 食品工程專碩一志愿中海洋309求調(diào)劑 +4 | 小張zxy張 2026-03-26 | 8/400 |
|
|
|
[考研]
 一志愿廈門大學化學學碩307求調(diào)劑
+10
|
y7czhao 2026-03-26 | 10/500 |
|
|
|
[考研] 346求調(diào)劑 一志愿070303有機化學 +3 | 蘿卜燉青菜 2026-03-28 | 3/150 |
|
|
|
[考研] 311求調(diào)劑 +3 | 希望上岸阿小楊 2026-03-23 | 3/150 |
|
|
|
[考研] 材料求調(diào)劑 一志愿哈工大總分298分，前三科223分 +5 | dongfang59 2026-03-27 | 5/250 |
|
|
|
[考研] 安徽大學專碩生物與醫(yī)藥專業(yè)(086000)324分，英語已過四六級，六級521，求調(diào)劑 +4 | 美味可樂雞翅 2026-03-26 | 4/200 |
|
|
|
[考研] 復試調(diào)劑，一志愿南農(nóng)083200食品科學與工程 +5 | XQTJZ 2026-03-26 | 5/250 |
|
|
|
[考研] 276求調(diào)劑。有半年電池和半年高分子實習經(jīng)歷 +10 | 材料學257求調(diào)劑 2026-03-23 | 11/550 |
|
|
|
[考研] 343求調(diào)劑 +4 | 贈我一本書 2026-03-23 | 4/200 |
|
|
|
[考研] 342求調(diào)劑 +3 | 加油a李zs 2026-03-26 | 3/150 |
|
|
|
[考研] 材料與化工304求B區(qū)調(diào)劑 +3 | 邱gl 2026-03-26 | 6/300 |
|
|
|
[考研] 289求調(diào)劑 +17 | 碩星赴 2026-03-23 | 17/850 |
|
|
|
[考研] 一志愿天津大學339材料與化工求調(diào)劑 +3 | 江往賣魚 2026-03-26 | 3/150 |
|
|
|
[論文投稿] 急發(fā)核心期刊論文 +3 | 賢達問津 2026-03-23 | 5/250 |
|