Fig. 4. Hot modulus of rupture(HMOR) at 1400℃ of the specimens for AS (A), ASM (B, C) and AM (D). In order to investigate the corrosion resistance of each specimen, a rotary corrosion test was conducted. The experiment was repeated 10 times after putting slag into the castable at 1650℃±50℃ for an hour, and the slag, of which the C/S was 5.8 (C/S=5.8), was collected at the work site. Fig. 5 shows the cross sections of the specimens. Slag penetration layers were not found in all the specimens. The corrosion resistance index of those specimens appeared to be A>B>C>D in order of numerical value. It is considered that the corrosion resistance of castables were improved due to the densification of fine structure during the expansion of volume due to the spinel formation after adding magnesia. |
回復(fù)此樓» 猜你喜歡
323求調(diào)劑
已經(jīng)有6人回復(fù)
-
一志愿北京化工大學(xué) 070300 學(xué)碩 336分 求調(diào)劑
已經(jīng)有4人回復(fù)
-
352求調(diào)劑
已經(jīng)有3人回復(fù)
-
一志愿東華大學(xué)化學(xué)070300，求調(diào)劑
已經(jīng)有8人回復(fù)
-
277材料科學(xué)與工程080500求調(diào)劑
已經(jīng)有7人回復(fù)
-
317求調(diào)劑
已經(jīng)有18人回復(fù)
-
293求調(diào)劑
已經(jīng)有5人回復(fù)
-
280分求調(diào)劑 一志愿085802
已經(jīng)有7人回復(fù)
-
0854電子信息求調(diào)劑
已經(jīng)有3人回復(fù)
-
263求調(diào)劑
已經(jīng)有4人回復(fù)
wanfuping
木蟲 (小有名氣)
- 翻譯EPI: 35
- 應(yīng)助: 0 (幼兒園)
- 金幣: 2378.1
- 紅花: 3
- 帖子: 243
- 在線: 329.2小時(shí)
- 蟲號(hào): 2050897
- 注冊(cè): 2012-10-09
- 性別: GG
- 專業(yè): 人工智能與知識(shí)工程
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-09-23 19:40:03
wanghao69: 金幣+12, 翻譯EPI+1, ★★★★★最佳答案, 非常非常感謝 2014-09-25 13:40:32
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-09-23 19:40:03
wanghao69: 金幣+12, 翻譯EPI+1, ★★★★★最佳答案, 非常非常感謝 2014-09-25 13:40:32
|
圖4 1400度時(shí)，AS (A), ASM (B, C) 和 AM (D)樣本的斷裂模量 為了研究每一樣本耐腐蝕性，進(jìn)行了旋轉(zhuǎn)腐蝕測(cè)試。在1650℃±50℃時(shí)將爐渣放入澆注材料1小時(shí)后，實(shí)進(jìn)行了驗(yàn)10次， 這里的爐渣，其C/S是5.8，是在現(xiàn)場(chǎng)收集的。 圖5展示了樣本的橫截面。樣本中沒有爐渣侵入層。按數(shù)量大小，這些樣本的耐腐蝕性指數(shù)為A>B>C>D 通常認(rèn)為，因增加氧化鎂后形成了尖晶石，在體積擴(kuò)展的時(shí)候，由于精細(xì)結(jié)構(gòu)的致密，澆注材料的耐腐蝕性增加了 |
2樓2014-09-23 16:35:55
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 wanghao69 的主題更新
| 2 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 一志愿北京化工大學(xué) 070300 學(xué)碩 336分 求調(diào)劑 +4 | vv迷 2026-03-22 | 4/200 |
|
|---|---|---|---|---|
|
|
[考研] 263求調(diào)劑 +4 | yqdszhdap－ 2026-03-22 | 4/200 |
|
|
|
[考研] 289求調(diào)劑 +7 | 懷瑾握瑜l 2026-03-20 | 7/350 |
|
|
[考研] 生物學(xué)調(diào)劑 +5 | Surekei 2026-03-21 | 5/250 |
|
|
|
[考研] 269專碩求調(diào)劑 +6 | 金恩貝 2026-03-21 | 6/300 |
|
|
|
[考研] 求調(diào)劑 +7 | Auroracx 2026-03-22 | 7/350 |
|
|
|
[考研] 354求調(diào)劑 +7 | Tyoumou 2026-03-18 | 10/500 |
|
|
|
[考研]
 一志愿東華大學(xué)控制學(xué)碩320求調(diào)劑
+3
|
Grand777 2026-03-21 | 3/150 |
|
|
|
[考研] 南昌大學(xué)材料專碩311分求調(diào)劑 +6 | 77chaselx 2026-03-20 | 6/300 |
|
|
|
[考研] 083200學(xué)碩321分一志愿暨南大學(xué)求調(diào)劑 +3 | innocenceF 2026-03-17 | 3/150 |
|
|
|
[考研] 材料 336 求調(diào)劑 +3 | An@. 2026-03-18 | 4/200 |
|
|
|
[考研] 一志愿華中科技大學(xué)，080502，354分求調(diào)劑 +5 | 守候夕陽CF 2026-03-18 | 5/250 |
|
|
|
[考研] 一志愿 西北大學(xué) ，070300化學(xué)學(xué)碩，總分287，雙非一本，求調(diào)劑。 +3 | 晨昏線與星海 2026-03-18 | 3/150 |
|
|
|
[考研] 308求調(diào)劑 +3 | 阿姐阿姐家啊 2026-03-18 | 3/150 |
|
|
|
[考研] 304求調(diào)劑 +7 | 司空. 2026-03-18 | 7/350 |
|
|
|
[考研] 350求調(diào)劑 +5 | weudhdk 2026-03-19 | 5/250 |
|
|
|
[考研] 290求調(diào)劑 +7 | ^O^乜 2026-03-19 | 7/350 |
|
|
|
[考研] 261求B區(qū)調(diào)劑，科研經(jīng)歷豐富 +3 | 牛奶很忙 2026-03-20 | 4/200 |
|
|
|
[考研] 328求調(diào)劑，英語六級(jí)551，有科研經(jīng)歷 +4 | 生物工程調(diào)劑 2026-03-16 | 12/600 |
|
|
|
[考研] 【同濟(jì)軟件】軟件（085405）考研求調(diào)劑 +3 | 2026eternal 2026-03-18 | 3/150 |
|