As seen in the photo, local peelings caused by structural spalling have appeared at the upper part of metal line in ASM (B). However, no spalling is found in ASM (C). This indicates the enhancement when compared with AS (A). Table 4 shows the comparison of physical properties and corrosion ratio between the AS (A) and ASM (C) after a field test in. The bulk densities of both specimens are similar to each other, but the apparent porosity in ASM (C) has been reduced 7% in comparison with the AS (A). The corrosion rate of ASM (C) has improved by about 10% in comparison with AS (A) .It is judged that the formation of spinel and CA6 has brought about the densification of the material during the use of magnesia-containing castables. Table 4. Comparison of physical properties & Corrosion ratio of AS(A) & ASM(C) after field test. Furthermore, the proper addition of microsilica into castables could reduce the spalling by suppressing the excessive formation of CA6 at movable surface, which resulted in the extension of life time of the steel ladle. |
回復(fù)此樓» 猜你喜歡
一志愿武理材料工程348求調(diào)劑
已經(jīng)有6人回復(fù)
-
08工科 320總分 求調(diào)劑
已經(jīng)有11人回復(fù)
-
一志愿華中農(nóng)業(yè)071010，總分320求調(diào)劑
已經(jīng)有6人回復(fù)
-
323求調(diào)劑
已經(jīng)有5人回復(fù)
-
284求調(diào)劑
已經(jīng)有5人回復(fù)
-
317求調(diào)劑
已經(jīng)有16人回復(fù)
-
287求調(diào)劑
已經(jīng)有9人回復(fù)
-
求調(diào)劑
已經(jīng)有6人回復(fù)
-
308求調(diào)劑
已經(jīng)有3人回復(fù)
-
環(huán)境學(xué)碩288求調(diào)劑
已經(jīng)有6人回復(fù)
wanfuping
木蟲(chóng) (小有名氣)
- 翻譯EPI: 35
- 應(yīng)助: 0 (幼兒園)
- 金幣: 2378.1
- 紅花: 3
- 帖子: 243
- 在線: 329.2小時(shí)
- 蟲(chóng)號(hào): 2050897
- 注冊(cè): 2012-10-09
- 性別: GG
- 專(zhuān)業(yè): 人工智能與知識(shí)工程
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-09-23 15:35:23
英語(yǔ)留級(jí)生: 金幣+12, 翻譯EPI+1, ★★★★★最佳答案 2014-09-25 13:38:49
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-09-23 15:35:23
英語(yǔ)留級(jí)生: 金幣+12, 翻譯EPI+1, ★★★★★最佳答案 2014-09-25 13:38:49
|
如圖所示, 由結(jié)構(gòu)散裂而致的局部剝離現(xiàn)象在ASM (B)中[液面線]的上端出現(xiàn)了。然而，在ASM (C)中沒(méi)有出現(xiàn)散烈現(xiàn)象。這表明，對(duì)比于AS(A)，ASM (C)提高了。表4展示了，經(jīng)歷一現(xiàn)場(chǎng)測(cè)試后，AS (A)和ASM (C)的物理性質(zhì)和腐蝕比率的對(duì)比情況。兩樣本的體積密度相似，但對(duì)比于AS(A),ASM(C)中的明顯孔隙減少了7%，而腐蝕速率增加了約10%。這就可判斷，在使用含鎂的澆注材料時(shí)，尖晶石和CA6的形成使其更加致密。 現(xiàn)場(chǎng)測(cè)試后，AS (A)和ASM (C)的物理性質(zhì)和腐蝕比率的對(duì)比 此外，通過(guò)抑制在移動(dòng)面上形成過(guò)量的CA6，在澆注材料中添加適量的硅粉可以減少散裂，從而延長(zhǎng)鋼水包的壽命。 注：[]中的我不能確定，請(qǐng)斟酌使用！ |
2樓2014-09-23 15:23:54
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 英語(yǔ)留級(jí)生 的主題更新
| 2 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 08工科 320總分 求調(diào)劑 +11 | 梨花珞晚風(fēng) 2026-03-17 | 11/550 |
|
|---|---|---|---|---|
|
[考研] 一志愿華中農(nóng)業(yè)071010，總分320求調(diào)劑 +5 | 困困困困坤坤 2026-03-20 | 6/300 |
|
|
|
[考研] 305分求調(diào)劑（食品工程） +4 | Sxy112 2026-03-21 | 6/300 |
|
|
|
[考研] 一志愿北京化工大學(xué) 070300 學(xué)碩 336分 求調(diào)劑 +3 | vv迷 2026-03-22 | 3/150 |
|
|
|
[考研] 0856材料專(zhuān)碩353求調(diào)劑 +4 | NIFFFfff 2026-03-20 | 4/200 |
|
|
|
[考研] 一志愿深大，0703化學(xué)，總分302，求調(diào)劑 +4 | 七月-七七 2026-03-21 | 4/200 |
|
|
|
[考研] 277材料科學(xué)與工程080500求調(diào)劑 +6 | 自由煎餅果子 2026-03-16 | 6/300 |
|
|
|
[考研] 316求調(diào)劑 +6 | 梁茜雯 2026-03-19 | 6/300 |
|
|
|
[考研] 070300化學(xué)319求調(diào)劑 +7 | 錦鯉0909 2026-03-17 | 7/350 |
|
|
|
[考研] 301求調(diào)劑 +10 | yy要上岸呀 2026-03-17 | 10/500 |
|
|
|
[考研] 083200學(xué)碩321分一志愿暨南大學(xué)求調(diào)劑 +3 | innocenceF 2026-03-17 | 3/150 |
|
|
|
[考研] 274求調(diào)劑 +10 | S.H1 2026-03-18 | 10/500 |
|
|
|
[考研] 294求調(diào)劑材料與化工專(zhuān)碩 +15 | 陌の森林 2026-03-18 | 15/750 |
|
|
|
[考研] 085600材料與化工 +8 | 安全上岸！ 2026-03-16 | 8/400 |
|
|
|
[考研] 材料學(xué)碩318求調(diào)劑 +5 | February_Feb 2026-03-19 | 5/250 |
|
|
|
[考研] 一志愿中國(guó)海洋大學(xué)，生物學(xué)，301分，求調(diào)劑 +5 | 1孫悟空 2026-03-17 | 6/300 |
|
|
|
[考研] 0703化學(xué)調(diào)劑 +4 | 18889395102 2026-03-18 | 4/200 |
|
|
|
[考研] 一志愿福大288有機(jī)化學(xué)，求調(diào)劑 +3 | 小木蟲(chóng)200408204 2026-03-18 | 3/150 |
|
|
|
[考研] 收復(fù)試調(diào)劑生 +4 | 雨后秋荷 2026-03-18 | 4/200 |
|
|
|
[考研] 0703化學(xué)調(diào)劑 +3 | 妮妮ninicgb 2026-03-17 | 3/150 |
|