wanglina金蟲 (正式寫手)
|
[求助]
不用種子層，氧化鋅納米棒陣列可以水熱合成嗎？
|
|
不用種子層，氧化鋅納米棒陣列可以水熱合成嗎？文獻是這樣做的，我重復(fù)的，沒長上�！� 文獻如下： Preparation of ZnO NRAs on Ni Foam. In this experiment, allthe chemicals were analytical grade and were used without further purification. Ahead of the experiment, the Ni foam substrate (1 × 1cm2) was ultrasonically washed with ethanol and water for 20 min each and then placed into the autoclave liners vertically. The reaction solution was prepared by mixing 0.015 M zinc nitrate hexahydrate and 0.015 M hexamethylenetetraamine (HMTA) together with 2 mL of ammonia in 70 mL of distilled water under constant magnetic stirring for 30 min. The reaction solution was then transferred into the autoclave liners and kept sealed at 90 °C for 24 h. After the reaction,the Ni foam coated with a white product was washed with deionized water, and thus the ZnO NRAs were obtained. 請教原因？ |
回復(fù)此樓» 猜你喜歡
求調(diào)劑
已經(jīng)有3人回復(fù)
-
化工學(xué)院（學(xué)院正式調(diào)劑群+聯(lián)系方式）
已經(jīng)有0人回復(fù)
-
無機化學(xué)論文潤色/翻譯怎么收費?
已經(jīng)有155人回復(fù)
-
化工學(xué)院（學(xué)院官方群）-院士團隊招生-學(xué)生自由度高-培養(yǎng)模式成熟高效
已經(jīng)有0人回復(fù)
-
黑龍江大學(xué)分析化學(xué)招調(diào)劑
已經(jīng)有0人回復(fù)
-
武漢高校國家級人才團隊招收材料，化學(xué)，紡織等專業(yè)碩士調(diào)劑生
已經(jīng)有26人回復(fù)
-
紡大化工學(xué)院（官方群）-院士團隊招生-學(xué)生自由度高發(fā)展好-培養(yǎng)模式成熟
已經(jīng)有0人回復(fù)
-
溫州大學(xué)化材學(xué)院王娟課題組招生
已經(jīng)有5人回復(fù)
-
學(xué)院官方群-院士團隊招生-學(xué)生自由度高-培養(yǎng)模式成熟已有10余名學(xué)生赴985海外深造
已經(jīng)有0人回復(fù)
-
武漢紡織大學(xué)化工學(xué)院官方群-院士團隊招生-學(xué)生自由度高-10余名學(xué)生赴985海外深造
已經(jīng)有0人回復(fù)
-
南昌航空大學(xué)蔣華麟教授課題組招收化學(xué)、環(huán)境、碳達峰碳中和及相關(guān)專業(yè)碩士信息
已經(jīng)有0人回復(fù)
» 本主題相關(guān)商家推薦: (我也要在這里推廣)
» 本主題相關(guān)價值貼推薦，對您同樣有幫助:
- WO3納米棒制備
已經(jīng)有7人回復(fù)
- ZnO納米棒的合成
已經(jīng)有14人回復(fù)
- 合成的金紅石TiO2納米棒陣列在做截面SEM時，為什么有時能看到陣列，有時候就是一團？
已經(jīng)有11人回復(fù)
- 關(guān)于制備ZnO納米線的問題
已經(jīng)有15人回復(fù)
- 請問納米棒陣列是幾維材料？
已經(jīng)有13人回復(fù)
- 水熱法制備納米四氧化三鐵求助�。�
已經(jīng)有36人回復(fù)
- 關(guān)于水熱法制備納米氧化鋅的溶液配制
已經(jīng)有14人回復(fù)
- 新手求助制備Au納米棒的方法，標題要長…………………………
已經(jīng)有27人回復(fù)
- znO納米桿水熱
已經(jīng)有17人回復(fù)
- 請問一些氧化鋅納米棒陣列制備上的問題
已經(jīng)有15人回復(fù)
- 水熱法制備Co3O4納米線，為何總是做不出來
已經(jīng)有13人回復(fù)
- 氧化鋅納米棒的制備
已經(jīng)有21人回復(fù)
- WO3水熱合成的看過來�。。�
已經(jīng)有9人回復(fù)
- 水熱法制zno納米棒陣列
已經(jīng)有11人回復(fù)
- 實驗室制備納米氧化鋅的具體步驟，我用來作催化劑！
已經(jīng)有5人回復(fù)
- 有關(guān)氧化鋅納米的問題
已經(jīng)有10人回復(fù)
- 水熱法合成氧化鋅納米線
已經(jīng)有9人回復(fù)
- 水熱法制備TiO2納米棒陣列
已經(jīng)有20人回復(fù)
- 水熱法合成單晶TiO2棒陣列
已經(jīng)有24人回復(fù)
- 電沉積ZnO納米棒
已經(jīng)有13人回復(fù)
- 水熱法合成氧化鋅納米球
已經(jīng)有18人回復(fù)
- 【求助】水熱法制備ZnO只得到黃色溶液
已經(jīng)有12人回復(fù)
forever23519
新蟲 (初入文壇)
- 應(yīng)助: 0 (幼兒園)
- 金幣: 59.6
- 帖子: 12
- 在線: 19.8小時
- 蟲號: 4262059
- 注冊: 2015-12-02
- 專業(yè): 電化學(xué)
2樓2018-11-13 13:04:16
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 wanglina 的主題更新
| 2 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 317分 一志愿南理工材料工程 本科湖工大 求調(diào)劑 +10 | 芋泥小鈴鐺 2026-03-28 | 10/500 |
|
|---|---|---|---|---|
|
[考研] 296求調(diào)劑 +6 | 彼岸t 2026-03-29 | 6/300 |
|
|
|
[考研] 340求調(diào)劑 +6 | Amber00 2026-03-26 | 6/300 |
|
|
|
[考研] 2026年華南師范大學(xué)歡迎化學(xué)，化工，生物，生醫(yī)工等專業(yè)優(yōu)秀學(xué)子加入！ +3 | llss0711 2026-03-28 | 6/300 |
|
|
|
[考研] 學(xué)碩274求調(diào)劑 +9 | Li李魚 2026-03-26 | 9/450 |
|
|
|
[考研] 315求調(diào)劑 +4 | akie... 2026-03-28 | 5/250 |
|
|
|
[考研] 312，生物學(xué)求調(diào)劑 +3 | 小譯同學(xué)abc 2026-03-28 | 3/150 |
|
|
|
[考研] 085701環(huán)境工程，267求調(diào)劑 +16 | minht 2026-03-26 | 16/800 |
|
|
|
[考研] 322求調(diào)劑 +4 | 我真的很想學(xué)習(xí) 2026-03-23 | 4/200 |
|
|
|
[考研] 0703化學(xué)一志愿南京師范大學(xué)303求調(diào)劑 +3 | zzffylgg 2026-03-24 | 3/150 |
|
|
|
[考研] 289求調(diào)劑 +17 | 碩星赴 2026-03-23 | 17/850 |
|
|
|
[考研] 281求調(diào)劑 +6 | Koxui 2026-03-24 | 7/350 |
|
|
|
[考研] 機械學(xué)碩總分317求調(diào)劑�。。�！ +4 | Acaciad 2026-03-25 | 4/200 |
|
|
|
[考研] 材料專碩 335 分求調(diào)劑 +4 | 拒絕冷暴力 2026-03-25 | 4/200 |
|
|
|
[考研] 26考研-291分-廈門大學(xué)（085601）-柔性電子學(xué)院材料工程專業(yè)求調(diào)劑 +3 | min3 2026-03-24 | 4/200 |
|
|
|
[考研] 302求調(diào)劑 +4 | 錦衣衛(wèi)藤椒 2026-03-25 | 4/200 |
|
|
|
[考研] 318求調(diào)劑 +3 | plum李子 2026-03-23 | 3/150 |
|
|
|
[考研]
 材料考研調(diào)劑生
+3
|
黃粱一夢千年 2026-03-24 | 3/150 |
|
|
|
[考研] 344求調(diào)劑 +3 | desto 2026-03-24 | 3/150 |
|
|
|
[考研] 336化工調(diào)劑 +4 | 王大坦1 2026-03-23 | 5/250 |
|