| 3 | 1/1 | 返回列表 |
| 查看: 440 | 回復(fù): 2 | |||
zouhengye銀蟲 (初入文壇)
|
[求助]
磁性測(cè)量表征的一段英語(yǔ)翻譯成漢語(yǔ)
|
| The magnetic susceptibility of compound 5 versus temperature is shown in Figure 8, the χMT value at 300K is 13.59 cm3 mol-1 K, it is close to the value expected for three Mn(II) (S = 5/2) noninteracting ions (13.125 cm3 mol-1 K, g = 2). This is corroborated by the continuous decrease of χMT upon cooling down to 11.96 cm3 mol-1 K at 80K. Below that temperature, the decrease is more abrupt, with χMT reaching a value of 4.47 cm3 mol-1 K at 2K, which is close to the spin - only (g = 2) value of 4.375 cm3 mol-1 K for a spin ground state S = 5/2. Additionally, a decrease in the low temperature χMT (T) data could also arise from zero-field splitting of the 6A1g ground state imposed by a distortion of the Mn2+ octahedron. The magnetic susceptibility above 10 K obeys the Curie-Weiss law with the Weiss constant, θ = -12.19 K, and Curie constant, C = 14.03 cm3 mol-1 K per Mn3 unit. The negative weiss constants indicate weak antiferromagnetic interactions between the Mn(II) centers. |
回復(fù)此樓» 猜你喜歡
求調(diào)劑
已經(jīng)有7人回復(fù)
-
275求調(diào)劑
已經(jīng)有6人回復(fù)
-
招08考數(shù)學(xué)
已經(jīng)有7人回復(fù)
-
303求調(diào)劑
已經(jīng)有6人回復(fù)
-
306求調(diào)劑
已經(jīng)有4人回復(fù)
-
求調(diào)劑
已經(jīng)有7人回復(fù)
-
考研調(diào)劑
已經(jīng)有4人回復(fù)
-
285求調(diào)劑
已經(jīng)有6人回復(fù)
-
一志愿北京化工大學(xué)070300 學(xué)碩336求調(diào)劑
已經(jīng)有7人回復(fù)
-
318求調(diào)劑
已經(jīng)有6人回復(fù)
風(fēng)云輕淡
新蟲 (初入文壇)
- 應(yīng)助: 0 (幼兒園)
- 金幣: 1518.5
- 帖子: 32
- 在線: 2.4小時(shí)
- 蟲號(hào): 3445350
- 注冊(cè): 2014-09-27
- 專業(yè): 心理學(xué)
★
zouhengye: 金幣+1, 翻譯EPI+1, ★有幫助, 文件過(guò)期，無(wú)法查看 2014-11-14 09:47:36
RXMCDM: 翻譯EPI-1, 求助者說(shuō)文件無(wú)法查看，如果你能看到，請(qǐng)復(fù)制后傳上來(lái)！ 2014-11-14 18:55:45
zouhengye: 金幣+1, 翻譯EPI+1, ★有幫助, 文件過(guò)期，無(wú)法查看 2014-11-14 09:47:36
RXMCDM: 翻譯EPI-1, 求助者說(shuō)文件無(wú)法查看，如果你能看到，請(qǐng)復(fù)制后傳上來(lái)！ 2014-11-14 18:55:45
|
點(diǎn)擊[https://pinyin.cn/1hS5y2xphw6] 查看這張圖片。[訪問(wèn)驗(yàn)證碼是：027804請(qǐng)妥善保管] [ 發(fā)自小木蟲客戶端 ] |
2樓2014-11-13 21:39:05
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
真強(qiáng)必勝: 金幣+2, 謝謝 2014-12-05 08:47:27
zouhengye(RXMCDM代發(fā)): 金幣+10, 多謝應(yīng)助！ 2014-12-20 16:55:48
真強(qiáng)必勝: 金幣+2, 謝謝 2014-12-05 08:47:27
zouhengye(RXMCDM代發(fā)): 金幣+10, 多謝應(yīng)助！ 2014-12-20 16:55:48
| 化合物5隨溫度變化的磁導(dǎo)率見圖8，在300 K的χMT值為13.59 cm3 mol-1 K，接近于三個(gè)無(wú)相互作用 Mn(II) (S = 5/2) 離子 (13.125 cm3 mol-1 K, g = 2)的磁矩預(yù)期值。這與降溫時(shí)χMT連續(xù)下降到80K的 11.96 cm3 mol-1 K相互印證。低于80K，下降變得更快，在2K， χMT 為 4.47 cm3 mol-1 K ，接近于純自旋 (g = 2) 值基態(tài) S = 5/2的 4.375 cm3 mol-1 K。另外， χMT (T) 曲線在低溫段的下降也由Mn2+八面體畸變?cè)斐傻?A1g 基態(tài)零場(chǎng)劈裂引起。10K以上的磁導(dǎo)率服從居里-外斯定律，外斯常數(shù) θ = -12.19 K， 每個(gè) Mn3單元的居里常數(shù)C = 14.03 cm3 mol-1 K。外斯常數(shù)為負(fù)，表明Mn(II)中心之間存在弱的反鐵磁作用。 |
3樓2014-11-19 14:47:45
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 zouhengye 的主題更新
| 3 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 能源材料化學(xué)課題組招收碩士研究生8-10名 +5 | 脫穎而出 2026-03-16 | 16/800 |
|
|---|---|---|---|---|
|
|
[考研] 生物學(xué)調(diào)劑 +4 | Surekei 2026-03-21 | 4/200 |
|
|
[考研] 280求調(diào)劑 +11 | 咕嚕曉曉 2026-03-18 | 12/600 |
|
|
|
[考研] 269專碩求調(diào)劑 +5 | 金恩貝 2026-03-21 | 5/250 |
|
|
|
[考研] 求調(diào)劑 +4 | 要好好無(wú)聊 2026-03-21 | 4/200 |
|
|
|
[考研] 0703化學(xué)調(diào)劑 +4 | 妮妮ninicgb 2026-03-21 | 4/200 |
|
|
|
[考研] 278求調(diào)劑 +9 | 煙火先于春 2026-03-17 | 9/450 |
|
|
|
[考研] 311求調(diào)劑 +3 | 勇敢的小吳 2026-03-20 | 3/150 |
|
|
|
[考研] 265求調(diào)劑 +3 | Jack?k?y 2026-03-17 | 3/150 |
|
|
|
[考研] 一志愿南京理工大學(xué)085701資源與環(huán)境302分求調(diào)劑 +4 | 葵梓衛(wèi)隊(duì) 2026-03-18 | 6/300 |
|
|
|
[考研] 288求調(diào)劑 +16 | 于海海海海 2026-03-19 | 16/800 |
|
|
|
[考研] A區(qū)線材料學(xué)調(diào)劑 +5 | 周周無(wú)極 2026-03-20 | 5/250 |
|
|
|
[考研] 289求調(diào)劑 +6 | 懷瑾握瑜l 2026-03-20 | 6/300 |
|
|
|
[考研] 材料與化工專碩調(diào)劑 +7 | heming3743 2026-03-16 | 7/350 |
|
|
|
[考研] 08工學(xué)調(diào)劑 +5 | 用戶573181 2026-03-20 | 5/250 |
|
|
|
[考研] 085410人工智能專碩317求調(diào)劑（0854都可以） +4 | xbxudjdn 2026-03-18 | 4/200 |
|
|
|
[考研] 材料學(xué)碩318求調(diào)劑 +5 | February_Feb 2026-03-19 | 5/250 |
|
|
|
[考研] 085600材料與化工調(diào)劑 324分 +10 | llllkkkhh 2026-03-18 | 12/600 |
|
|
|
[考研] 材料工程專碩調(diào)劑 +5 | 204818@lcx 2026-03-17 | 6/300 |
|
|
|
[考研] 333求調(diào)劑 +3 | 文思客 2026-03-16 | 7/350 |
|