446739074新蟲 (初入文壇)
|
[求助]
鋰電改性,如何證明是摻雜而非包覆?需要哪些測(cè)試分析? 已有4人參與
|
||
| 我做的是Ce摻雜三元鋰離子電池正極材料,審稿意見如下:“If the Ce is doped in the sample, how to identify the amount of Ce on the sample? How to identify whether Ce is doped on the sample or not? If the amount of Ce is very small, it could be also coated on the sample rather than doping. The authors showed the XRD pattern to prove the Ce doping effect, but do you have other measurement or evidences for the doping effect.” 我只做了XRD測(cè)試,晶胞參數(shù)分析發(fā)現(xiàn)了變化,但審稿人認(rèn)為不夠。請(qǐng)問我應(yīng)該從哪些方面下手去解釋,或者我應(yīng)該補(bǔ)做些什么測(cè)試可以充分證明是摻雜而非包覆? |
鋰電 |
銀蟲 (小有名氣)
版主 (著名寫手)
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 085600材料與化工調(diào)劑 +10 | kikiki7 2026-03-30 | 10/500 |
|
|---|---|---|---|---|
|
[考研] 285求調(diào)劑 +6 | AZMK 2026-03-29 | 9/450 |
|
|
[考研] 調(diào)劑 +4 | GK72 2026-03-30 | 4/200 |
|
|
[考研] 材料與化工(0856)304求B區(qū)調(diào)劑 +3 | 邱gl 2026-03-30 | 7/350 |
|
|
[考研] 083000環(huán)境科學(xué)與工程調(diào)劑,總分281 +3 | 橙子(勝意) 2026-03-30 | 3/150 |
|
|
[考研] 309求調(diào)劑 +15 | 誰不是少年 2026-03-29 | 15/750 |
|
|
[考研] 求調(diào)劑 +7 | 青春裁為三截 2026-03-29 | 7/350 |
|
|
[考研] 一志愿211,335分,0856,求調(diào)劑院校和導(dǎo)師 +7 | 傾____蕭 2026-03-27 | 8/400 |
|
|
[考研] 一志愿南航 335分 | 0856 | GPA 4.07 | 有科研經(jīng)歷 +8 | cccchenso 2026-03-29 | 8/400 |
|
|
[考研] 298求調(diào)劑 +3 | 種圣賜 2026-03-29 | 3/150 |
|
|
[考研] 343求調(diào)劑 +5 | 愛羈絆 2026-03-28 | 5/250 |
|
|
[考研] 347求調(diào)劑 +3 | 山頂見α 2026-03-25 | 3/150 |
|
|
[考研] 070300求調(diào)劑306分 +4 | 26要上岸 2026-03-27 | 4/200 |
|
|
[材料工程] 一志愿C9材料與化工專業(yè)總分300求調(diào)劑 +8 | 曼111 2026-03-24 | 9/450 |
|
|
[考研] 265求調(diào)劑 +8 | 小木蟲085600 2026-03-27 | 8/400 |
|
|
[考研] 一志愿上海理工能源動(dòng)力(085800)310分求調(diào)劑 +3 | zhangmingc 2026-03-27 | 4/200 |
|
|
[考研] 289求調(diào)劑 +17 | 碩星赴 2026-03-23 | 17/850 |
|
|
[考研] 309求調(diào)劑 +4 | gajsj 2026-03-25 | 5/250 |
|
|
[考研] 292求調(diào)劑 +4 | 鵝鵝鵝額額額額?/a> 2026-03-24 | 4/200 |
|
|
[考研] 344求調(diào)劑 +3 | desto 2026-03-24 | 3/150 |
|