求翻譯這段話
|
||
|
Before each experiment, the [1,3-(pr)2im]Br was dried at 75 C under reduced pressure. The PAs were prepared by the following general procedure: as an example for the preparation of PA10aI, 0.10 g (1.70 9 10-4 mol) of diacid 8, 0.0338 g (1.70 9 10-4 mol) of diamine 9a and 0.25 g of [1,3-(pr)2im]Br were placed in a porcelain dish and the mixture was ground completely for 5 min, then 0.11 mL (4.26 9 10-4 mol) of TPP was added, and the mixture was ground for 3 min. The reaction mixture was irradiated in the microwave oven for a period of 40 ? 40 ? 20 s at 70% of power level. The resulting viscous solution was poured into 30 mL of methanol, filtered, and dried under vacuum to give 0.118 g (88%) of PA10aI. |
回復此樓» 猜你喜歡
329求調(diào)劑
已經(jīng)有5人回復
-
材料求調(diào)劑一志愿哈工大324
已經(jīng)有8人回復
-
286求調(diào)劑
已經(jīng)有7人回復
-
083000學碩274求調(diào)劑
已經(jīng)有7人回復
-
311求調(diào)劑
已經(jīng)有8人回復
-
一志愿C9材料與化工專業(yè)總分300求調(diào)劑
已經(jīng)有9人回復
-
311求調(diào)劑
已經(jīng)有3人回復
-
291求調(diào)劑
已經(jīng)有6人回復
-
一志愿廈門大學化學學碩307求調(diào)劑
已經(jīng)有9人回復
-
286求調(diào)劑
已經(jīng)有10人回復
hool 
捐助貴賓 (正式寫手)
木星之王
- 翻譯EPI: 17
- 應助: 8 (幼兒園)
- 金幣: 1913.9
- 散金: 11304
- 紅花: 2
- 帖子: 690
- 在線: 1465.1小時
- 蟲號: 536507
- 注冊: 2008-03-31
- 性別: GG
- 專業(yè): 金屬功能材料
【答案】應助回帖
|
每次實驗前均對[1,3-(pr)2im]Br進行減壓干燥。 PAs是通過以下方式制備的：以制備PA10aI, 0.10 g (1.70 9 10-4 mol) of diacid 8為例，首先將0.0338克二元胺和0.25克[1,3-(pr)2im]Br共同放置于磁碟中，并混合研磨5分鐘。然后加入0.11毫升的(4.26 9 10-4 摩爾)的TPP，再繼續(xù)研磨3分鐘。再將混合物放在微波爐中在70%強度下輻照40 ? 40 ? 20 s。最后， 將獲得的粘稠液體倒入30毫升的甲醇中過濾，然后在真空環(huán)境中干燥，即可獲得0.118克的PA10aI。 |
2樓2015-04-07 13:21:20
武漢一心一譯 
捐助貴賓 (著名寫手)
- 翻譯EPI: 502
- 應助: 8 (幼兒園)
- 金幣: 2283.1
- 散金: 5914
- 紅花: 32
- 帖子: 1665
- 在線: 321.9小時
- 蟲號: 3587652
- 注冊: 2014-12-10
- 性別: GG
- 專業(yè): 高分子合成化學
【答案】應助回帖
商家已經(jīng)主動聲明此回帖可能含有宣傳內(nèi)容
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
大四寫論文: 金幣+30, 翻譯EPI+1, ★★★很有幫助 2015-04-08 08:40:08
大四寫論文: 金幣+30, 翻譯EPI+1, ★★★很有幫助 2015-04-08 08:40:08
|
每項實驗開始前，[1,3-(pr)2im]溴都在低壓，75攝氏度的條件下烘干。 同時，通過以下通用的程序提前制備好對氨基水楊酸：作為制備PA10aI的例子，首先在蒸發(fā)皿中放入0.10 g的二酸8(1.70 9 10-4 mol)，0.0338 g的二元胺(1.70 9 10-4 mol)，以及0.25 g溴[1,3-(pr)2im]進行混合，將混合物充分研磨5分鐘，然后加入0.11毫升的磷酸三苯酯（4.26 9 10-4 mol），在詞研磨3分鐘。然后將已經(jīng)發(fā)生反應的混合物放入微波爐，以70%的微波功率對其進行輻射，時長控制在40 ? 40 ? 20 s。 將產(chǎn)生的粘性溶液導入30ml的甲醇，然后進行過濾，在真空條件下進行烘干，可以產(chǎn)出0.118g濃度為88%的PA10aI。 |
3樓2015-04-07 13:24:21
相關版塊跳轉
我要訂閱樓主 大四寫論文 的主題更新
| 3 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 311求調(diào)劑 +8 | lin0039 2026-03-26 | 8/400 |
|
|---|---|---|---|---|
|
|
[考研] 085404求調(diào)劑，總分309，本科經(jīng)歷較為豐富 +4 | 來財aa 2026-03-25 | 4/200 |
|
|
[考研] 315分求調(diào)劑 +7 | 26考研上岸版26 2026-03-26 | 7/350 |
|
|
|
[考研] 295材料工程專碩求調(diào)劑 +6 | 1428151015 2026-03-27 | 6/300 |
|
|
|
[考研] 求調(diào)劑 +8 | 張zz111 2026-03-27 | 9/450 |
|
|
|
[考研] 085602 307分 求調(diào)劑 +6 | 不知道叫什么！ 2026-03-26 | 6/300 |
|
|
|
[考研] 材料與化工（0856）304求B區(qū)調(diào)劑 +7 | 邱gl 2026-03-27 | 7/350 |
|
|
|
[考研] 085600材料與化工調(diào)劑 +10 | A-哆啦Z夢 2026-03-23 | 16/800 |
|
|
|
[考研] 0856調(diào)劑 +5 | 求求讓我有書讀?/a> 2026-03-26 | 6/300 |
|
|
|
[考研] 化學308分求調(diào)劑 +8 | 你好明天你好 2026-03-23 | 9/450 |
|
|
|
[考研] 324求調(diào)劑 +5 | hanamiko 2026-03-26 | 5/250 |
|
|
|
[考研] 321求調(diào)劑 +5 | 材料cailiao 2026-03-21 | 5/250 |
|
|
|
[考研] 324求調(diào)劑 +4 | wysyjs25 2026-03-21 | 4/200 |
|
|
|
[考研] 271求調(diào)劑 +6 | 生如夏花… 2026-03-22 | 6/300 |
|
|
|
[考研] 材料專碩 335 分求調(diào)劑 +4 | 拒絕冷暴力 2026-03-25 | 4/200 |
|
|
|
[考研] 285求調(diào)劑 +3 | AZMK 2026-03-24 | 3/150 |
|
|
|
[考研] 086003食品工程求調(diào)劑 +6 | 淼淼111 2026-03-24 | 6/300 |
|
|
|
[考研] 289材料與化工（085600）B區(qū)求調(diào)劑 +4 | 這么名字咋樣 2026-03-22 | 5/250 |
|
|
|
[考研] 上海電力大學材料防護與新材料重點實驗室招收調(diào)劑研究生（材料、化學、電化學，環(huán)境） +4 | 我愛學電池 2026-03-23 | 4/200 |
|
|
|
[考研] 求調(diào)劑 +5 | Zhangbod 2026-03-21 | 7/350 |
|