求助翻譯一段摘要。英譯中。
|
|
| Abstract: In this paper, we fabricated a high-strength self-supporting NaA zeolite membrane from a geopolymer membrane through in situ hydrothermal transformation processing. The surface and inner amorphous geopolymer membrane was converted into the zeolite crystal phase after the hydrothermal process was applied, and the volume of the micropores of the hydrothermal sample changed from 0 to 0.049 cc/g after the hydrothermal process. We preliminarily studied the practicability and preparation of a self-supporting NaA zeolite membrane with a high compressive strength (approximately 57 MPa) for desalination through a pervaporation process. The results showed that the self-supporting NaA zeolite membranes exhibited improved high sodium ion rejection (approximately 99.5%) as the thickness gradually increased to a certain value (about 9.4 mm), and the flux (0.42 kg m-2 h-1 at 25ºC) gradually increased to 3.86 kg m-2 h-1 as the pervaporation temperature increased to 90ºC. |
回復(fù)此樓» 猜你喜歡
295材料工程專碩求調(diào)劑
已經(jīng)有8人回復(fù)
-
求調(diào)劑
已經(jīng)有8人回復(fù)
-
293求調(diào)劑
已經(jīng)有5人回復(fù)
-
279求調(diào)劑
已經(jīng)有8人回復(fù)
-
328求調(diào)劑
已經(jīng)有8人回復(fù)
-
322求調(diào)劑：一志愿湖南大學(xué) 材料與化工（085600），已過六級(jí)。
已經(jīng)有9人回復(fù)
-
307求調(diào)劑
已經(jīng)有17人回復(fù)
-
286求調(diào)劑
已經(jīng)有5人回復(fù)
-
085600 295分求調(diào)劑
已經(jīng)有6人回復(fù)
-
287求調(diào)劑
已經(jīng)有13人回復(fù)
baoshanqiu
至尊木蟲 (著名寫手)
- 翻譯EPI: 204
- 應(yīng)助: 103 (高中生)
- 金幣: 15293.5
- 紅花: 41
- 帖子: 1611
- 在線: 431.6小時(shí)
- 蟲號(hào): 3856202
- 注冊: 2015-05-08
- 性別: GG
- 專業(yè): 胃腸道免疫相關(guān)疾病
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★
paul9979: 金幣+30, 翻譯EPI+1, ★★★★★最佳答案 2015-06-17 21:58:40
paul9979: 金幣+30, 翻譯EPI+1, ★★★★★最佳答案 2015-06-17 21:58:40
| 摘要：在本文中，我們用地質(zhì)聚合膜經(jīng)原位水溫轉(zhuǎn)化制造了一種高強(qiáng)度自身支持NaA沸石分子篩膜。在水溫作用下，表面和內(nèi)部無定形的地質(zhì)聚合膜轉(zhuǎn)變?yōu)榉惺肿雍Y晶相，水溫樣品的微孔體積由0變?yōu)?.049 cc/g。我們初步測試了以高耐壓強(qiáng)度 （近57 MPa）制備自身支持NaA沸石分子篩膜通過全蒸發(fā)作用脫鹽及其可行性。結(jié)果表明這種自身支持NaA沸石分子篩膜隨著厚度逐漸增加到一定值（近 9.4 mm)，當(dāng)全蒸發(fā)溫度有25攝氏度增加到90攝氏度，流量由0.42kg/平方米/小時(shí)逐漸增加到3.86kg/平方米/小時(shí)， 其表現(xiàn)出高排鈉離子能力（近 99.5%)。 |
2樓2015-06-16 22:32:31
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 paul9979 的主題更新
| 2 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 332求調(diào)劑 +6 | @MZB382400 2026-03-28 | 6/300 |
|
|---|---|---|---|---|
|
[考研] 0703一志愿9，初試成績：338，四六級(jí)已過，有科研經(jīng)歷，求調(diào)劑！ +6 | Zuhui0306 2026-03-25 | 6/300 |
|
|
|
[考研] 生物技術(shù)與工程 +7 | 1294608413 2026-03-25 | 8/400 |
|
|
|
[考研] 材料與化工272求調(diào)劑 +21 | 阿斯蒂芬2004 2026-03-28 | 21/1050 |
|
|
|
[考研] 317求調(diào)劑 +10 | 蛋黃咸肉粽 2026-03-26 | 10/500 |
|
|
|
[考研] 一志愿南航 335分 | 0856 | GPA 4.07 | 有科研經(jīng)歷 +8 | cccchenso 2026-03-29 | 8/400 |
|
|
|
[考研] 材料科學(xué)與工程求調(diào)劑 +6 | 深V宿舍吧 2026-03-29 | 6/300 |
|
|
|
[考研] 【求調(diào)劑】085601材料工程專碩 | 總分272 | +7 | 腳滑的守法公民 2026-03-27 | 7/350 |
|
|
|
[考研] 311（085601）求調(diào)劑 +4 | liziyeyeye 2026-03-28 | 4/200 |
|
|
|
[考研] 283求調(diào)劑 +3 | A child 2026-03-28 | 3/150 |
|
|
|
[考研] 070300求調(diào)劑306分 +4 | 26要上岸 2026-03-27 | 4/200 |
|
|
|
[考研] 一志愿南京航空航天大學(xué)材料學(xué)碩求調(diào)劑 +3 | @taotao 2026-03-28 | 3/150 |
|
|
|
[考研] 085701環(huán)境工程求調(diào)劑 +9 | 多久上課 2026-03-27 | 9/450 |
|
|
|
[考研] 086000調(diào)劑 +3 | 7901117076 2026-03-26 | 3/150 |
|
|
|
[考研] 一志愿南師大0703化學(xué) 275求調(diào)劑 +4 | Ripcord上岸 2026-03-27 | 4/200 |
|
|
|
[考研] 求調(diào)劑 +3 | 劉柯@ 2026-03-24 | 4/200 |
|
|
|
[考研] 一志愿鄭大085600，310分求調(diào)劑 +5 | 李瀟可 2026-03-26 | 5/250 |
|
|
|
[考研] 求調(diào)劑 +6 | 林之夕 2026-03-24 | 6/300 |
|
|
|
[考研] 081200-11408-276學(xué)碩求調(diào)劑 +4 | 崔wj 2026-03-26 | 4/200 |
|
|
|
[考研] 085601求調(diào)劑總分293英一數(shù)二 +4 | 鋼鐵大炮 2026-03-24 | 4/200 |
|