你真丑新蟲 (初入文壇)
|
[求助]
求大神翻譯外文摘要 謝謝 已有2人參與
|
| The work focuses on the syntheses of red inorganic ceramic pigments by inclusion of hematite in a fumed silica matrix. Leaching tests in boiling solutions of concentrated (36 wt%) hydrochloric acid demonstrated that, starting from mixtures of fumed silica and synthetic goethite, the occlusion of hematite occurs by calcination at 1150 –1200°C for 2– 4 h. Better results were obtained by using fumed silica having surface area ranging from 300 to 400 m2/g. A continuos change in colour was measured by comparing L-a-b values of the calcined samples and more information were obtained by the Kubelka- Munk absorption function. Because its chemical and thermal stability, the obtained heteromorphic pigment may be considered a suitable red pigment for ceramic manufacturing by fast firing cycles. |
回復(fù)此樓» 猜你喜歡
281求調(diào)劑（0805）
已經(jīng)有8人回復(fù)
-
環(huán)境領(lǐng)域全國(guó)重點(diǎn)實(shí)驗(yàn)室招收博士1-2名
已經(jīng)有3人回復(fù)
-
材料專碩306英一數(shù)二
已經(jīng)有10人回復(fù)
-
301求調(diào)劑
已經(jīng)有6人回復(fù)
-
一志愿天津大學(xué)化學(xué)工藝專業(yè)（081702）315分求調(diào)劑
已經(jīng)有7人回復(fù)
-
302求調(diào)劑
已經(jīng)有6人回復(fù)
-
26博士申請(qǐng)
已經(jīng)有3人回復(fù)
-
268求調(diào)劑
已經(jīng)有3人回復(fù)
-
311求調(diào)劑
已經(jīng)有10人回復(fù)
-
被我言中：新模板不強(qiáng)調(diào)格式了，假專家開始管格式了
已經(jīng)有4人回復(fù)
peterflyer 
木蟲之王 (文學(xué)泰斗)
peterflyer
- 應(yīng)助: 20282 (院士)
- 金幣: 146144
- 紅花: 1374
- 帖子: 93091
- 在線: 7694.3小時(shí)
- 蟲號(hào): 1482829
- 注冊(cè): 2011-11-08
- 性別: GG
- 專業(yè): 功能陶瓷
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ...
感謝參與，應(yīng)助指數(shù) +1
飛翔fx: 金幣+2 2015-08-08 11:53:29
你真丑: 金幣+50, ★★★很有幫助 2015-09-15 10:31:19
感謝參與，應(yīng)助指數(shù) +1
飛翔fx: 金幣+2 2015-08-08 11:53:29
你真丑: 金幣+50, ★★★很有幫助 2015-09-15 10:31:19
| 本工作的重點(diǎn)放在通過(guò)向二氧化硅氣溶膠基質(zhì)中添加赤鐵礦來(lái)合成紅色無(wú)機(jī)陶瓷顏料的方法上面。在煮沸了的濃鹽酸(36 wt%)中的浸出實(shí)驗(yàn)表明，以二氧化硅氣溶膠和人工合成的針鐵礦的混合物為原料在 1150~1200°C 的溫度下煅燒 2~4 小時(shí)就生成赤鐵礦。使用比表面積300~400m2/g的二氧化硅氣溶膠為原料時(shí)可得到更好的結(jié)果。通過(guò)比較煅燒樣品的L-a-b的數(shù)值可以連續(xù)地測(cè)量產(chǎn)品顏色的變化，更多的信息還可通過(guò) Kubelka- Munk 吸附函數(shù)來(lái)獲得。因?yàn)楫a(chǎn)品的化學(xué)和熱學(xué)的良好穩(wěn)定性，這種性能特異的顏料也許適合用于具有快速燒制周期生產(chǎn)工藝的陶瓷所需的顏料。 |
2樓2015-08-04 13:24:53
lyf452433605
銅蟲 (正式寫手)
- 應(yīng)助: 0 (幼兒園)
- 金幣: 28.8
- 散金: 555
- 紅花: 3
- 帖子: 462
- 在線: 94.9小時(shí)
- 蟲號(hào): 1189094
- 注冊(cè): 2011-01-13
- 性別: GG
- 專業(yè): 金屬材料
| 本工作的重點(diǎn)在于通過(guò)向二氧化硅氣溶膠基質(zhì)中添加赤鐵礦來(lái)合成紅色無(wú)機(jī)陶瓷顏料。在煮沸的濃鹽酸(36 wt%)中的浸泡的實(shí)驗(yàn)表明，以二氧化硅氣溶膠和人工合成的針鐵礦的混合物為原料在 1150~1200°C 的溫度下煅燒 2~4 小時(shí)就生成赤鐵礦。使用比表面積300~400m2/g的二氧化硅氣溶膠為原料時(shí)可得到更好的結(jié)果。通過(guò)比較煅燒樣品的L-a-b值可以連續(xù)地測(cè)量產(chǎn)品顏色的變化，更多的信息還可通過(guò) Kubelka- Munk 吸附函數(shù)來(lái)獲得。因?yàn)楫a(chǎn)品的化學(xué)和熱學(xué)的穩(wěn)定性，這種性能特異的顏料也許適合用于具有快速燒制周期生產(chǎn)工藝的陶瓷所需的顏料。 |
3樓2015-08-11 17:00:00
818james
銅蟲 (著名寫手)
- 應(yīng)助: 59 (初中生)
- 金幣: 7611.1
- 紅花: 17
- 帖子: 1455
- 在線: 878.1小時(shí)
- 蟲號(hào): 3719023
- 注冊(cè): 2015-03-08
【答案】應(yīng)助回帖
|
The work focuses on the syntheses of red inorganic ceramic pigments by inclusion of hematite in a fumed silica matrix. Leaching tests in boiling solutions of concentrated (36 wt%) hydrochloric acid demonstrated that, starting from mixtures of fumed silica and synthetic goethite, the occlusion of hematite occurs by calcination at 1150 –1200°C for 2– 4 h. Better results were obtained by using fumed silica having surface area ranging from 300 to 400 m2/g. A continuos change in colour was measured by comparing L-a-b values of the calcined samples and more information were obtained by the Kubelka- Munk absorption function. Because its chemical and thermal stability, the obtained heteromorphic pigment may be considered a suitable red pigment for ceramic manufacturing by fast firing cycles. 本工作重點(diǎn)是將赤鐵礦(粉)包在薰過(guò)的硅石基質(zhì)中以合成紅色無(wú)機(jī)陶瓷顏料。沸濃鹽酸(36 wt%)浸出試驗(yàn)表明，將薰過(guò)的硅石和人工合成針鐵礦的混合物在 1150~1200°C 的溫度下煅燒 2~4 小時(shí)就可發(fā)生赤鐵礦吸留（包藏）。使用比表面積300~400m2/g的硅石效果更好。 比較煅燒樣品的L-a-b的數(shù)值可測(cè)出產(chǎn)品顏色的連續(xù)變化，更多的信息可通過(guò) Kubelka- Munk 吸附函數(shù)獲得。由于(產(chǎn)品的)抗腐蝕耐高溫（化學(xué)和熱學(xué)的良好穩(wěn)定性），(所獲得的)這種多晶型顏料可認(rèn)為是一種適用于陶瓷快速燒制生產(chǎn)的紅色顏料。 |
4樓2015-08-12 02:20:49
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 你真丑 的主題更新
| 4 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 301求調(diào)劑 +4 | A_JiXing 2026-03-16 | 4/200 |
|
|---|---|---|---|---|
|
|
[考研] 326求調(diào)劑 +5 | 上岸的小葡 2026-03-15 | 6/300 |
|
|
[考研] 08工科 320總分 求調(diào)劑 +4 | 梨花珞晚風(fēng) 2026-03-17 | 4/200 |
|
|
|
[考研] 289求調(diào)劑 +6 | 步川酷紫123 2026-03-11 | 6/300 |
|
|
|
[考研] 東南大學(xué)364求調(diào)劑 +5 | JasonYuiui 2026-03-15 | 5/250 |
|
|
|
[基金申請(qǐng)] 國(guó)自科面上基金字體 +6 | iwuli 2026-03-12 | 7/350 |
|
|
|
[考研] 一志愿985，本科211，0817化學(xué)工程與技術(shù)319求調(diào)劑 +5 | Liwangman 2026-03-15 | 5/250 |
|
|
|
[考研] 318求調(diào)劑 +3 | Yanyali 2026-03-15 | 3/150 |
|
|
|
[考研] 321求調(diào)劑 +5 | 大米飯！ 2026-03-15 | 5/250 |
|
|
|
[考研] 0703化學(xué)調(diào)劑 290分有科研經(jīng)歷，論文在投 +7 | 膩膩gk 2026-03-14 | 7/350 |
|
|
|
[考研] 0856求調(diào)劑 +3 | 劉夢(mèng)微 2026-03-15 | 3/150 |
|
|
|
[考研] 070305求調(diào)劑 +3 | mlpqaz03 2026-03-14 | 4/200 |
|
|
|
[考研] 材料工程327求調(diào)劑 +3 | xiaohe12w 2026-03-11 | 3/150 |
|
|
|
[考研] 本科南京大學(xué)一志愿川大藥學(xué)327 +3 | 麥田耕者 2026-03-14 | 3/150 |
|
|
|
[考研] 材料080500調(diào)劑求收留 +3 | 一顆meteor 2026-03-13 | 3/150 |
|
|
|
[考研] 工科，求調(diào)劑 +3 | 我887 2026-03-11 | 3/150 |
|
|
|
[考研] 315求調(diào)劑 +9 | 小羊小羊_ 2026-03-11 | 10/500 |
|
|
|
[考研] 310求調(diào)劑 +3 | 【上上簽】 2026-03-11 | 3/150 |
|
|
|
[考研] 工科278分求調(diào)劑 +5 | 周慢熱啊 2026-03-12 | 7/350 |
|
|
|
[考研] 085600材料與化工 309分請(qǐng)求調(diào)劑 +7 | dtdxzxx 2026-03-12 | 8/400 |
|