By electrophoretic deposition of TiO2 colloidal suspensions into the pores of an AAM, ordered TiO2 nanowire arrays can be obtained In a typical procedure, TTIP is dissolved in ethanol at room temperature, and glacial acetic acid mixed with deionized water and ethanol is added under pH = 2-3 with nitric acid. TiO2 nanotubes can also be obtained using the sol-gel method by templating with an AAM and other organic compounds. For example, when an AAM is used as the template, a thin layer of TiO2 sol on the wall of the pores of the AAM is first prepared by sucking TiO2 sol into the pores of the AAM and removing it under vacuum; TiO2 nanowires are obtained after the sol is fully developed and the AAM is removed. The AAM was hydrolyzed by water vapor over a HCl solution for 24 h, air-dried at room temperature, and then calcined in a furnace at 673 K for 2 h and cooled to room temperature with a temperature ramp of 2 °C/h. 請問這幾句話怎么翻譯  |
回復(fù)此樓» 猜你喜歡
求調(diào)劑
已經(jīng)有6人回復(fù)
-
085600材料與化工調(diào)劑
已經(jīng)有4人回復(fù)
-
327求調(diào)劑
已經(jīng)有4人回復(fù)
-
309求調(diào)劑
已經(jīng)有8人回復(fù)
-
一志愿南航 335分 | 0856 | GPA 4.07 | 有科研經(jīng)歷
已經(jīng)有8人回復(fù)
-
求化學(xué)調(diào)劑
已經(jīng)有5人回復(fù)
-
085600，材料與化工321分求調(diào)劑
已經(jīng)有10人回復(fù)
-
0703 化學(xué) 求調(diào)劑，一志愿山東大學(xué) 342 分
已經(jīng)有5人回復(fù)
-
一志愿南開大學(xué)0710生物學(xué)359求調(diào)劑
已經(jīng)有3人回復(fù)
-
085600，專業(yè)課化工原理，320分求調(diào)劑
已經(jīng)有4人回復(fù)
sqlg888
鐵蟲 (正式寫手)
- SFL-EPI: 1
- 應(yīng)助: 163 (高中生)
- 金幣: 4544.2
- 紅花: 27
- 帖子: 995
- 在線: 191.8小時
- 蟲號: 4176864
- 注冊: 2015-10-27
- 專業(yè): 民族藥學(xué)
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★
感謝參與，應(yīng)助指數(shù) +1
jina123: 金幣+8, ★★★★★最佳答案 2016-01-02 13:46:39
感謝參與，應(yīng)助指數(shù) +1
jina123: 金幣+8, ★★★★★最佳答案 2016-01-02 13:46:39
|
通過二氧化鈦的膠體懸浮液在AAM孔中的電泳淀積，可以得到有序的TiO2納米線陣列， 在經(jīng)典的方法中，室溫下將TTIP溶于乙醇（A），將冰醋酸與去離子水、乙醇混合用硝酸控制pH=2-3。（B） TiO2納米管也可以使用溶膠-凝膠法，通過用的AAM模板和其他有機化合物模板化輔助獲得。 例如，用AAM作模板，首先制備TiO2溶膠吸吮到AAM模板孔中并在真空下去除，TiO2溶膠在AAM的孔的壁上形成薄層;溶膠充分生長后，除去AAM模板，得到二氧化鈦納米線。 水解AAM可用HCl溶液水蒸汽24小時，在室溫下空氣干燥，隨后在爐中煅燒（673 K，2小時）并冷卻到室溫（升溫速率在2℃/小時）。 |
2樓2015-12-31 16:15:00
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 jina123 的主題更新
| 2 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 275求調(diào)劑 +15 | Micky11223 2026-03-25 | 20/1000 |
|
|---|---|---|---|---|
|
|
[考研] 291求調(diào)劑 +7 | Y-cap 2026-03-29 | 8/400 |
|
|
|
[考研] 299求調(diào)劑 +10 | 15188958825 2026-03-25 | 10/500 |
|
|
|
[考研] 327求調(diào)劑 +6 | 汲亦昊 2026-03-29 | 6/300 |
|
|
|
[考研] 070300化學(xué)354求調(diào)劑 +6 | 101次希望 2026-03-28 | 6/300 |
|
|
|
[考研] 332求調(diào)劑 +8 | 蕉蕉123 2026-03-28 | 8/400 |
|
|
|
[考研] 298求調(diào)劑 +4 | 種圣賜 2026-03-28 | 4/200 |
|
|
|
[考研] 322求調(diào)劑 +7 | 宋明欣 2026-03-27 | 7/350 |
|
|
|
[考研] 311求調(diào)劑 +3 | 希望上岸阿小楊 2026-03-23 | 3/150 |
|
|
|
[考研] 295求調(diào)劑 +5 | 1428151015 2026-03-27 | 6/300 |
|
|
|
[有機交流]
高溫高壓反應(yīng)求助
 10+4
|
chibby 2026-03-25 | 4/200 |
|
|
[考研] 材料292調(diào)劑 +12 | 橘頌思美人 2026-03-23 | 12/600 |
|
|
|
[考研] 一志愿華東理工大學(xué)081700，初試分數(shù)271 +6 | kotoko_ik 2026-03-23 | 7/350 |
|
|
|
[考研] 085601 材料工程 313分 求調(diào)劑 +5 | Ong3 2026-03-27 | 5/250 |
|
|
|
[考研] 求調(diào)劑 +6 | 林之夕 2026-03-24 | 6/300 |
|
|
|
[考研] 調(diào)劑 +4 | 柚柚yoyo 2026-03-26 | 4/200 |
|
|
|
[考研] 打過很多競賽，085406控制工程300分，求調(diào)劑 +3 | askeladz 2026-03-26 | 3/150 |
|
|
|
[考研] 309求調(diào)劑 +4 | gajsj 2026-03-25 | 5/250 |
|
|
|
[考研] 機械學(xué)碩總分317求調(diào)劑�。。�！ +4 | Acaciad 2026-03-25 | 4/200 |
|
|
|
[考研] 080500求調(diào)劑 +3 | zzzzfan 2026-03-24 | 3/150 |
|