求助：翻譯摘要
|
|||
|
摘要：以原子比為3﹕1的Fe粉和Si粉球磨20 h后加入一定量的Cu，在(1000±30)℃，20 MPa的壓力下通過(guò)熱壓燒結(jié)的方法制備了致密的Fe3Si-Cu復(fù)合材料。通過(guò)浸泡腐蝕和電化學(xué)腐蝕兩種方法討論了加入不同質(zhì)量分?jǐn)?shù)Cu（5%，10%）的Fe3Si-Cu復(fù)合材料在NaOH溶液中的腐蝕行為。結(jié)果表明，加入5%Cu的復(fù)合材料具有更好的耐腐蝕性能。Fe3Si-5%Cu的浸泡腐蝕速率要小，腐蝕的要輕一些；Fe3Si-5%Cu 和Fe3Si-10%Cu兩種材料在不同摩爾濃度的NaOH溶液中的極化曲線都出現(xiàn)了鈍化，有寬泛的鈍化區(qū)域，明顯的鈍化平臺(tái)，兩種材料在不同摩爾濃度的NaOH溶液中的腐蝕是一種均勻的全面腐蝕，沒(méi)有出現(xiàn)點(diǎn)蝕現(xiàn)象。比較極化曲線的特征值，F(xiàn)e3Si-5%Cu在0.7 mol/l的NaOH溶液中的自腐蝕電位更正，自腐蝕電流小，并且最先進(jìn)入鈍化區(qū)，在鈍化區(qū)域，維鈍電流也小。 關(guān)鍵詞：球磨；熱壓燒結(jié)Fe3Si-Cu；Cu含量；浸泡腐蝕；電化學(xué)腐蝕 |
回復(fù)此樓» 猜你喜歡
求調(diào)劑
已經(jīng)有4人回復(fù)
-
一志愿北京化工大學(xué)070300 學(xué)碩336求調(diào)劑
已經(jīng)有6人回復(fù)
-
考研調(diào)劑
已經(jīng)有3人回復(fù)
-
能源材料化學(xué)課題組招收碩士研究生8-10名
已經(jīng)有16人回復(fù)
-
318求調(diào)劑
已經(jīng)有5人回復(fù)
-
285求調(diào)劑
已經(jīng)有5人回復(fù)
-
306求調(diào)劑
已經(jīng)有3人回復(fù)
-
354求調(diào)劑
已經(jīng)有10人回復(fù)
-
303求調(diào)劑
已經(jīng)有5人回復(fù)
-
環(huán)境學(xué)碩288求調(diào)劑
已經(jīng)有4人回復(fù)
» 搶金幣啦！回帖就可以得到:
-
坐標(biāo)上海，誠(chéng)征女友，非常 著急，私信必回
+1/461
-
香港中文大學(xué)（深圳）靳羽華教授交叉實(shí)驗(yàn)室招募2026年材料學(xué)博士生（光致變色）
+2/154
-
中國(guó)電氣裝備集團(tuán)研究院招收AI+材料等相關(guān)崗位實(shí)習(xí)生
+1/88
-
文獻(xiàn)分享，歡迎引用
+1/83
-
雙一流南京醫(yī)科大學(xué)招計(jì)算機(jī)、AI、統(tǒng)計(jì)、生物信息等方向26年9月入學(xué)博士
+1/81
-
春天就該逛吃逛吃
+1/81
-
溫州大學(xué)呂晶晶課題組2026年招生
+1/76
-
有沒(méi)有在香港的蟲友啊
+1/72
-
青島高校 研究生招生
+1/47
-
Alicat 層流壓差質(zhì)量流量控制器在新型硅碳負(fù)極流化床的應(yīng)用- 艾里卡特（Alicat）
+3/46
-
江蘇科技大學(xué)能源材料化學(xué)課題組郭興梅教授招收博士研究生1-2名
+1/45
-
歡迎交流咨詢
+1/42
-
吲哚美辛原料藥合成交流
+1/35
-
西安某大學(xué)能源化工新材料研發(fā)項(xiàng)目組接收2026級(jí)調(diào)劑研究生-計(jì)算機(jī)類
+1/32
-
1
+1/31
-
招聘科研助理——儲(chǔ)能方向（儲(chǔ)能、流體傳熱、CFD模擬）
+1/16
-
計(jì)算機(jī)(11408)考研361分求調(diào)劑
+1/10
-
南京醫(yī)科大學(xué)-膜蛋白結(jié)構(gòu)與功能課題組-招收2026級(jí)博士研究生
+1/9
-
河南大學(xué)龔和貴教授2026年博士研究生招生
+1/5
-
生物技術(shù)工程+326，求調(diào)劑！
+1/3
zerohead
禁蟲 (職業(yè)作家)
- 翻譯EPI: 466
- 應(yīng)助: 1 (幼兒園)
- 貴賓: 0.301
- 金幣: 8727.8
- 帖子: 3768
- 在線: 471.7小時(shí)
- 蟲號(hào): 1041741
usth(金幣+10, 翻譯EPI+1): 謝謝，贈(zèng)分晚了，對(duì)不起。 2011-01-25 01:09:24
|
以原子比為3﹕1的Fe粉和Si粉球磨20 h后加入一定量的Cu，在(1000±30)℃，20 MPa的壓力下通過(guò)熱壓燒結(jié)的方法制備了致密的Fe3Si-Cu復(fù)合材料。 With a Fe to S atomic ratio of 3, the mixture of the powders was ball ground for 20 h before adding a certain amount of Cu. Then dense Fe3Si-Cu composite material was prepared by hot-pressing of the resultant mixture under 20 MPa and (1000±30)℃. |
2樓2011-01-15 05:25:33
3樓2011-01-15 17:15:32
4樓2011-01-15 17:16:40
slz146
木蟲 (正式寫手)
- 翻譯EPI: 75
- 應(yīng)助: 0 (幼兒園)
- 貴賓: 0.055
- 金幣: 1657.8
- 帖子: 713
- 在線: 225.5小時(shí)
- 蟲號(hào): 1097156
usth(金幣+40): 非常感謝，最近工作忙沒(méi)來(lái)得及上網(wǎng)。贈(zèng)分晚了，對(duì)不起啊。 2011-01-25 01:11:02
|
abstract: With an atomic ratio of Fe/S=3,the mixture of the powders was ball milled for 20 h before adding some Cu.We have prepared dense Fe3Si-Cu composite material by the method of Hot-pressing Sinter-roasting under 20 MPa and (1000±30)℃.Also we discussed the corrosion behavior of Fe3Si-Cu composite material with different concentrations of Cu（5%，10%）in NaOH solution by two methods of static immersing corrosion and electrochemical corrosion.It turned out that the composite material with 5%Cu had better corrosion resistant.The speed of static immersing corrosion of Fe3Si-5%Cu was less,the extent of corrosion was also less.The polarization curves of Fe3Si-5%Cu and Fe3Si-10%Cu composite material appeared passivation in different molar concentrations of NaOH solution,and there was a broad area of passivation and apparently inactive platform.The corrosion of the two kinds of composite material was evenly rounded corrosion in different molar concentrations of NaOH solution.There was no pitting phenomenon appearing.Compared with characteristic values of the polarization curves,corrosion potential of Fe3Si-5%Cu revised in 0.7 mol/l of NaOH solution,its electric current of corrosion potential is small,and it went to area of passivation first .In area of passivation,maintaining passivity current was also small. keyword：ball mill，F(xiàn)e3Si-Cu by Hot-pressing Sinter-roasting,Cu content,static immersing corrosion,electrochemical corrosion |
5樓2011-01-16 10:39:51
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 usth 的主題更新
| 5 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 一志愿北京化工大學(xué)070300 學(xué)碩336求調(diào)劑 +4 | vv迷 2026-03-21 | 6/300 |
|
|---|---|---|---|---|
|
|
[考研] 285求調(diào)劑 +5 | ytter 2026-03-22 | 5/250 |
|
|
|
[考研] 286求調(diào)劑 +10 | Faune 2026-03-21 | 10/500 |
|
|
|
[考研]
 一志愿東華大學(xué)控制學(xué)碩320求調(diào)劑
+3
|
Grand777 2026-03-21 | 3/150 |
|
|
|
[考研] 考研化學(xué)學(xué)碩調(diào)劑，一志愿985 +5 | 張vvvv 2026-03-15 | 7/350 |
|
|
[考研] 求調(diào)劑 +5 | 十三加油 2026-03-21 | 5/250 |
|
|
|
[考研] 311求調(diào)劑 +3 | 勇敢的小吳 2026-03-20 | 3/150 |
|
|
|
[考研] 299求調(diào)劑 +5 | shxchem 2026-03-20 | 7/350 |
|
|
|
[考研] 22 350 本科985求調(diào)劑，求老登收留 +3 | 李軼男003 2026-03-20 | 3/150 |
|
|
|
[考研] 070300化學(xué)319求調(diào)劑 +7 | 錦鯉0909 2026-03-17 | 7/350 |
|
|
|
[考研] 307求調(diào)劑 +10 | 冷笙123 2026-03-17 | 10/500 |
|
|
|
[考研] 304求調(diào)劑 +6 | 曼殊2266 2026-03-18 | 6/300 |
|
|
|
[考研] 一志愿中海洋材料工程專碩330分求調(diào)劑 +8 | 小材化本科 2026-03-18 | 8/400 |
|
|
|
[考研] 一志愿南京理工大學(xué)085701資源與環(huán)境302分求調(diào)劑 +4 | 葵梓衛(wèi)隊(duì) 2026-03-18 | 6/300 |
|
|
|
[考研] 一志愿武漢理工材料工程專碩調(diào)劑 +9 | Doleres 2026-03-19 | 9/450 |
|
|
|
[考研] 求調(diào)劑，一志愿:南京航空航天大學(xué)大學(xué) ，080500材料科學(xué)與工程學(xué)碩，總分289分 +4 | @taotao 2026-03-19 | 4/200 |
|
|
|
[考研] 求調(diào)劑 +3 | eation27 2026-03-20 | 3/150 |
|
|
|
[考研] 招收調(diào)劑碩士 +4 | lidianxing 2026-03-19 | 12/600 |
|
|
|
[考研] 286求調(diào)劑 +6 | lemonzzn 2026-03-16 | 10/500 |
|
|
|
[考研] 326求調(diào)劑 +5 | 上岸的小葡 2026-03-15 | 6/300 |
|