[求助]
合成檸檬酸根修飾的磁性納米粒子時遇到的問題
|
|||
|
文獻上的制備方法： Magnetite(Fe3O4) particles were prepared by co-precipitation of FeCl2 and FeCl3 (1:2 molar ratio) by the addition of NH4OH. In a typical reaction, 0.86 g FeCl2 and 2.35 g FeCl3 were mixed in 40 ml water and heated to 80º C under argon in a three-necked flask. While vigorously stirring the reaction mixture, 5 ml of NH4OH was introduced by syringe and the heating continued for thirty minutes. After that, 1g of citric acid (CA) in 2ml water was introduced, the temperature raised to 95º C and the stirring continued for an additional ninety minutes. A small aliquot of the reaction mixture was withdrawn, diluted to twice its volume and placed on a 0.5 Tesla magnet in a vial. At the point when the particles did not settle down under the influence of the magnet, the colloidal solution was stable. The as-formed reaction product contained an excess of citric acid. Therefore, the nanoparticle dispersion was subjected to dialysis against water in a 12-14 kD cut-off cellulose membrane (Spectrum Laboratories, Inc., USA) for 72 hours to remove the excess unbound CA. The citric acid coated magnetic particles are abbreviated as MP-CA. 我的疑問： 反應在較高溫度下進行了很長時間(至少2小時)，體系一直在通氬氣，為了保證內部氣壓不至于過高，肯定要有出氣孔，這這么高溫度和這么長時間下，體系的水幾乎都揮發(fā)沒了，請問這個問題如何處理？ 謝謝，盼指導！ |
回復此樓» 猜你喜歡
招生負責_院士團隊_學生高自由度成長_擅長學生培養(yǎng)
已經有5人回復
-
溫州大學招收2026年入學博士研究生（化學、材料、環(huán)境）
已經有10人回復
-
金屬材料論文潤色/翻譯怎么收費?
已經有299人回復
-
非晶合金
已經有2人回復
-
院士團隊-每屆學生都優(yōu)秀-高自由度-團隊氛圍好
已經有0人回復
-
求調劑
已經有3人回復
-
化工學院（學院正式調劑群+聯(lián)系方式）
已經有0人回復
-
化工學院（學院官方群）-院士團隊招生-學生自由度高-培養(yǎng)模式成熟高效
已經有0人回復
-
黑龍江大學分析化學招調劑
已經有0人回復
-
武漢高校國家級人才團隊招收材料，化學，紡織等專業(yè)碩士調劑生
已經有26人回復
-
紡大化工學院（官方群）-院士團隊招生-學生自由度高發(fā)展好-培養(yǎng)模式成熟
已經有0人回復
» 本主題相關商家推薦: (我也要在這里推廣)
» 本主題相關價值貼推薦，對您同樣有幫助:
- 金納米粒子修飾后溶液中出現(xiàn)絮狀物
已經有9人回復
- 我用共沉淀法合成四氧化三鐵磁性納米，合成好之后加入檸檬酸還是會聚沉呢？
已經有24人回復
- 為什么合成出來的鎳納米粒子沒有磁性
已經有13人回復
- 【討論】關于金納米粒子合成的問題
已經有46人回復
- 【討論】檸檬酸根包被的金納米粒子 這句話怎么理解？
已經有9人回復
- 【求助】金銀合金納米粒子合成遇到的問題
已經有15人回復
- 【求助】納米金表面修飾---檸檬酸根和CTAB
已經有22人回復
- 【請教】磁性納米材料Fe3O4/Al2O3的合成中的問題
已經有24人回復
toy000
木蟲 (著名寫手)
- 應助: 13 (小學生)
- 金幣: 10046.6
- 散金: 6
- 紅花: 2
- 帖子: 1165
- 在線: 277.8小時
- 蟲號: 1112808
- 注冊: 2010-10-02
- 性別: GG
- 專業(yè): 應用高分子化學與物理
8樓2012-05-25 12:41:21
refnew
專家顧問 (知名作家)
-
專家經驗: +181 - MN-EPI: 4
- 應助: 678 (博士)
- 貴賓: 0.577
- 金幣: 9465.7
- 散金: 229
- 紅花: 54
- 帖子: 6391
- 在線: 1613.5小時
- 蟲號: 33447
- 注冊: 2003-12-31
- 性別: GG
- 專業(yè): 納米生物學
- 管轄: 微米和納米
2樓2012-05-05 10:13:33
3樓2012-05-05 10:22:48
refnew
專家顧問 (知名作家)
-
專家經驗: +181 - MN-EPI: 4
- 應助: 678 (博士)
- 貴賓: 0.577
- 金幣: 9465.7
- 散金: 229
- 紅花: 54
- 帖子: 6391
- 在線: 1613.5小時
- 蟲號: 33447
- 注冊: 2003-12-31
- 性別: GG
- 專業(yè): 納米生物學
- 管轄: 微米和納米
4樓2012-05-05 10:46:12
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 274求調劑 +6 | 顧九笙要謙虛 2026-03-24 | 6/300 |
|
|---|---|---|---|---|
|
[考研]
 材料與化工考研調劑
+8
|
孅華 2026-03-22 | 8/400 |
|
|
|
[考研] 294求調劑材料與化工專碩 +17 | 陌の森林 2026-03-18 | 17/850 |
|
|
|
[考研] 生物技術與工程 +3 | 1294608413 2026-03-25 | 3/150 |
|
|
|
[考研] 284求調劑 +14 | Zhao anqi 2026-03-22 | 14/700 |
|
|
|
[考研] 086003食品工程求調劑 +6 | 淼淼111 2026-03-24 | 6/300 |
|
|
|
[考研] 295求調劑 +6 | 一志愿京區(qū)211 2026-03-18 | 8/400 |
|
|
|
[考研] 289求調劑 +10 | 碩星赴 2026-03-23 | 10/500 |
|
|
|
[考研] B區(qū)考研調劑 +4 | yqdszhdap－ 2026-03-22 | 5/250 |
|
|
|
[考研] 08工學調劑 +12 | 用戶573181 2026-03-20 | 17/850 |
|
|
|
[考研] 0856材料專碩353求調劑 +6 | NIFFFfff 2026-03-20 | 6/300 |
|
|
|
[有機交流]
有機合成求助
 20+3
|
FENGSHUJEI 2026-03-23 | 5/250 |
|
|
|
[考研]
 085404電子信息284分求調劑
+4
|
13659058978 2026-03-24 | 4/200 |
|
|
|
[考研] 279分求調劑 一志愿211 +18 | chaojifeixia 2026-03-19 | 20/1000 |
|
|
|
[考研] 一志愿南京理工大學085701資源與環(huán)境302分求調劑 +5 | 葵梓衛(wèi)隊 2026-03-18 | 7/350 |
|
|
|
[基金申請] 山東省面上項目限額評審 +4 | 石瑞0426 2026-03-19 | 4/200 |
|
|
|
[考研] 材料與化工（0856）304求 B區(qū) 調劑 +3 | 邱gl 2026-03-21 | 3/150 |
|
|
|
[考研] 求調劑一志愿南京航空航天大學289分 +3 | @taotao 2026-03-19 | 3/150 |
|
|
|
[考研] 一志愿南理工085701環(huán)境302求調劑院校 +3 | 葵梓衛(wèi)隊 2026-03-20 | 3/150 |
|
|
|
[考研] 085410人工智能專碩317求調劑（0854都可以） +4 | xbxudjdn 2026-03-18 | 4/200 |
|