彎曲試驗(yàn)技術(shù)相關(guān)的，翻譯英文部分，謝謝 For this test, specimens with thickness a and width b are to be prepared, the edges of which may be rounded on the tension side to a radius of 1-2 mm.For plates and sections the specimen thickness a is equal to the product thickness t. For product thicknesses thicknesses exceeding 25 mm the thickness may be reduced by machining the compression side of the bend specimen to not less than 25 mm. To perform this test, the test specimen is bent in a continuous operation as shown in Figure 2.13 and using a mandrel of specified radius D/2 until the prescribed bending angle α is reached or the initial incipient fracture occurs. For normal strength steels D/2 = 2 ⋅ a, for higher strength steels D/2 = 3 ⋅ a. The test shall be satisfactory if the prescribed bending angle is achieved without incipient fracture. If, when the specimen is unclamped, it springs back, the bending operation need not be repeated. |
回復(fù)此樓» 猜你喜歡
263求調(diào)劑
已經(jīng)有4人回復(fù)
-
石河子大學(xué)（211、雙一流）碩博研究生長(zhǎng)期招生公告
已經(jīng)有3人回復(fù)
-
一志愿西安交通大學(xué)材料工程專業(yè) 282分求調(diào)劑
已經(jīng)有13人回復(fù)
-
北科281學(xué)碩材料求調(diào)劑
已經(jīng)有6人回復(fù)
-
328求調(diào)劑，英語(yǔ)六級(jí)551，有科研經(jīng)歷
已經(jīng)有10人回復(fù)
-
298求調(diào)劑
已經(jīng)有6人回復(fù)
-
310求調(diào)劑
已經(jīng)有4人回復(fù)
-
311求調(diào)劑
已經(jīng)有6人回復(fù)
-
307求調(diào)劑
已經(jīng)有11人回復(fù)
-
材料與化工085600，總分304，本科有兩篇sci參與，求調(diào)劑
已經(jīng)有5人回復(fù)
reko34
木蟲 (正式寫手)
- 翻譯EPI: 132
- 應(yīng)助: 117 (高中生)
- 金幣: 4794.2
- 散金: 22
- 紅花: 12
- 帖子: 780
- 在線: 417.4小時(shí)
- 蟲號(hào): 3055206
- 注冊(cè): 2014-03-15
- 性別: GG
- 專業(yè): 機(jī)械測(cè)試?yán)碚撆c技術(shù)
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ...
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-07-18 09:40:59
huangguaha: 金幣+100, 翻譯EPI+1, ★★★★★最佳答案, 非常感謝 2014-07-22 11:00:09
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-07-18 09:40:59
huangguaha: 金幣+100, 翻譯EPI+1, ★★★★★最佳答案, 非常感謝 2014-07-22 11:00:09
|
為試驗(yàn)準(zhǔn)備厚度a、寬度b的樣件，拉伸側(cè)的邊緣可倒半徑1-2mm的圓角。對(duì)于板和截面，試件厚度a等于產(chǎn)品厚度t。產(chǎn)品厚度超過25mm時(shí)，可以通過加工擠壓側(cè)將厚度減到小于25mm。 根據(jù)圖2.13所示的連續(xù)操作彎曲試件，使用半徑D/2的芯軸直到達(dá)到預(yù)定的彎曲角a或發(fā)生早期斷裂。對(duì)普通強(qiáng)度鋼D/2=2⋅a，對(duì)高強(qiáng)度鋼D/2=3⋅a。如果達(dá)到預(yù)定彎曲角而沒有出現(xiàn)早期斷裂，試驗(yàn)滿足要求。如果裝夾松開，試件彈回，不需要重復(fù)彎曲操作。 |
2樓2014-07-18 09:32:35
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 huangguaha 的主題更新
| 2 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 315分，誠(chéng)求調(diào)劑，材料與化工085600 +3 | 13756423260 2026-03-22 | 3/150 |
|
|---|---|---|---|---|
|
[考研]
 一志愿東華大學(xué)化學(xué)070300，求調(diào)劑
+6
|
2117205181 2026-03-21 | 7/350 |
|
|
|
[考研] 考研調(diào)劑 +4 | 來好運(yùn)來來來 2026-03-21 | 4/200 |
|
|
|
[考研] 0856材料專碩353求調(diào)劑 +4 | NIFFFfff 2026-03-20 | 4/200 |
|
|
|
[考研] 326求調(diào)劑 +5 | 諾貝爾化學(xué)獎(jiǎng)覬?/a> 2026-03-15 | 8/400 |
|
|
|
[考研] 求調(diào)劑 +3 | 13341 2026-03-20 | 3/150 |
|
|
|
[考研] 求助 +5 | 夢(mèng)里的無言 2026-03-21 | 6/300 |
|
|
|
[考研] 302求調(diào)劑 +12 | 呼呼呼。。。。 2026-03-17 | 12/600 |
|
|
|
[考研] 求調(diào)劑 +3 | .m.. 2026-03-21 | 4/200 |
|
|
|
[考研] 265求調(diào)劑 +12 | 梁梁校校 2026-03-19 | 14/700 |
|
|
|
[考研] 材料學(xué)學(xué)碩080502 337求調(diào)劑-一志愿華中科技大學(xué) +4 | 順順順mr 2026-03-18 | 5/250 |
|
|
|
[考研] 一志愿天津大學(xué)化學(xué)工藝專業(yè)（081702）315分求調(diào)劑 +12 | yangfz 2026-03-17 | 12/600 |
|
|
|
[考研] 295求調(diào)劑 +4 | 一志愿京區(qū)211 2026-03-18 | 6/300 |
|
|
|
[考研] 藥學(xué)383 求調(diào)劑 +3 | 藥學(xué)chy 2026-03-15 | 5/250 |
|
|
|
[考研] 0856調(diào)劑，是學(xué)校就去 +8 | sllhht 2026-03-19 | 9/450 |
|
|
|
[考研] 求調(diào)劑 +3 | 暗涌afhb 2026-03-16 | 3/150 |
|
|
|
[考研] 081700化工學(xué)碩調(diào)劑 +3 | 【1】 2026-03-16 | 3/150 |
|
|
|
[考研] 0703化學(xué)調(diào)劑 +5 | pupcoco 2026-03-17 | 8/400 |
|
|
|
[考研] 085600材料與化工求調(diào)劑 +6 | 緒幸與子 2026-03-17 | 6/300 |
|
|
|
[考研] 【同濟(jì)軟件】軟件（085405）考研求調(diào)劑 +3 | 2026eternal 2026-03-18 | 3/150 |
|