[求助]
英譯漢
|
||
|
彎曲試驗(yàn)技術(shù)相關(guān)的，翻譯英文部分，謝謝 For this test, specimens with thickness a and width b are to be prepared, the edges of which may be rounded on the tension side to a radius of 1-2 mm.For plates and sections the specimen thickness a is equal to the product thickness t. For product thicknesses thicknesses exceeding 25 mm the thickness may be reduced by machining the compression side of the bend specimen to not less than 25 mm. To perform this test, the test specimen is bent in a continuous operation as shown in Figure 2.13 and using a mandrel of specified radius D/2 until the prescribed bending angle α is reached or the initial incipient fracture occurs. For normal strength steels D/2 = 2 ⋅ a, for higher strength steels D/2 = 3 ⋅ a. The test shall be satisfactory if the prescribed bending angle is achieved without incipient fracture. If, when the specimen is unclamped, it springs back, the bending operation need not be repeated. |
回復(fù)此樓» 猜你喜歡
323求調(diào)劑
已經(jīng)有6人回復(fù)
-
一志愿北京化工大學(xué) 070300 學(xué)碩 336分 求調(diào)劑
已經(jīng)有4人回復(fù)
-
352求調(diào)劑
已經(jīng)有3人回復(fù)
-
一志愿東華大學(xué)化學(xué)070300，求調(diào)劑
已經(jīng)有8人回復(fù)
-
277材料科學(xué)與工程080500求調(diào)劑
已經(jīng)有7人回復(fù)
-
317求調(diào)劑
已經(jīng)有18人回復(fù)
-
293求調(diào)劑
已經(jīng)有5人回復(fù)
-
280分求調(diào)劑 一志愿085802
已經(jīng)有7人回復(fù)
-
0854電子信息求調(diào)劑
已經(jīng)有3人回復(fù)
-
263求調(diào)劑
已經(jīng)有4人回復(fù)
reko34
木蟲 (正式寫手)
- 翻譯EPI: 132
- 應(yīng)助: 117 (高中生)
- 金幣: 4794.2
- 散金: 22
- 紅花: 12
- 帖子: 780
- 在線: 417.4小時(shí)
- 蟲號(hào): 3055206
- 注冊(cè): 2014-03-15
- 性別: GG
- 專業(yè): 機(jī)械測(cè)試?yán)碚撆c技術(shù)
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ★ ...
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-07-18 09:40:59
huangguaha: 金幣+100, 翻譯EPI+1, ★★★★★最佳答案, 非常感謝 2014-07-22 11:00:09
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-07-18 09:40:59
huangguaha: 金幣+100, 翻譯EPI+1, ★★★★★最佳答案, 非常感謝 2014-07-22 11:00:09
|
為試驗(yàn)準(zhǔn)備厚度a、寬度b的樣件，拉伸側(cè)的邊緣可倒半徑1-2mm的圓角。對(duì)于板和截面，試件厚度a等于產(chǎn)品厚度t。產(chǎn)品厚度超過(guò)25mm時(shí)，可以通過(guò)加工擠壓側(cè)將厚度減到小于25mm。 根據(jù)圖2.13所示的連續(xù)操作彎曲試件，使用半徑D/2的芯軸直到達(dá)到預(yù)定的彎曲角a或發(fā)生早期斷裂。對(duì)普通強(qiáng)度鋼D/2=2⋅a，對(duì)高強(qiáng)度鋼D/2=3⋅a。如果達(dá)到預(yù)定彎曲角而沒有出現(xiàn)早期斷裂，試驗(yàn)滿足要求。如果裝夾松開，試件彈回，不需要重復(fù)彎曲操作。 |
2樓2014-07-18 09:32:35
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 huangguaha 的主題更新
| 2 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 298求調(diào)劑 +6 | 上岸6666@ 2026-03-20 | 6/300 |
|
|---|---|---|---|---|
|
[考研] 環(huán)境學(xué)碩288求調(diào)劑 +6 | 皮皮皮123456 2026-03-22 | 6/300 |
|
|
|
[考研] 319求調(diào)劑 +4 | 小力氣珂珂 2026-03-20 | 4/200 |
|
|
|
[考研] 384求調(diào)劑 +3 | 子系博 2026-03-22 | 4/200 |
|
|
|
[考研] 考研調(diào)劑 +3 | 呼呼？~+123456 2026-03-21 | 3/150 |
|
|
|
[考研] 307求調(diào)劑 +3 | 余意卿 2026-03-18 | 3/150 |
|
|
|
[考研] 299求調(diào)劑 +4 | 某某某某位 2026-03-21 | 4/200 |
|
|
|
[考研] 279求調(diào)劑 +5 | 紅衣隱官 2026-03-21 | 5/250 |
|
|
|
[考研] 085601調(diào)劑 358分 +3 | zzzzggh 2026-03-20 | 4/200 |
|
|
|
[考研] 一志愿 西北大學(xué) ，070300化學(xué)學(xué)碩，總分287，雙非一本，求調(diào)劑。 +4 | 晨昏線與星海 2026-03-19 | 4/200 |
|
|
|
[考研] 一志愿西南交通 專碩 材料355 本科雙非 求調(diào)劑 +5 | 西南交通專材355 2026-03-19 | 5/250 |
|
|
|
[考研]
 295復(fù)試調(diào)劑
+8
|
簡(jiǎn)木ChuFront 2026-03-19 | 8/400 |
|
|
|
[考研] 一志愿 南京航空航天大學(xué)大學(xué) ，080500材料科學(xué)與工程學(xué)碩 +5 | @taotao 2026-03-20 | 5/250 |
|
|
|
[考研] 353求調(diào)劑 +3 | 拉鉤不許變 2026-03-20 | 3/150 |
|
|
|
[考研] 261求B區(qū)調(diào)劑，科研經(jīng)歷豐富 +3 | 牛奶很忙 2026-03-20 | 4/200 |
|
|
|
[考研] 081700化工學(xué)碩調(diào)劑 +3 | 【1】 2026-03-16 | 3/150 |
|
|
|
[考研] 材料工程專碩調(diào)劑 +5 | 204818@lcx 2026-03-17 | 6/300 |
|
|
|
[考研] 材料專碩306英一數(shù)二 +10 | z1z2z3879 2026-03-16 | 13/650 |
|
|
|
[考研] 有沒有道鐵/土木的想調(diào)劑南林，給自己招師弟中～ +3 | TqlXswl 2026-03-16 | 7/350 |
|
|
|
[考研] 333求調(diào)劑 +3 | 文思客 2026-03-16 | 7/350 |
|