| The same measurements were conducted for the castables fired at 1500°C for 5 hours without any constraint in order to compare the effects of expansion free conditions with those of the constrained ones. For the corrosion resistance tests, the structural constraint was imposed using the same high-mechanical strength castable mentioned above. For this evaluation, the alumina-CAC castable was firstly shaped as shown in Figure 2 and, after its curing (50°C/24h), drying (110°C/24h) and sintering (1500°C/5h) steps, the alumina-magnesia castable was moulded inside its inner hole. After pre-firing the materials (sample + constrained material) at 600°C/5h, the corrosion experiment was carried out for 5 hours at 1500°C using 10g of a high-FeOx steel ladle slag (Table 1). The same testing conditions were applied for the nonconstrained castables (without any alumina- CAC castable surrounding them). |
回復(fù)此樓» 猜你喜歡
調(diào)劑申請
已經(jīng)有7人回復(fù)
-
環(huán)境工程297分求調(diào)劑一志愿杭高院
已經(jīng)有8人回復(fù)
-
070300化學(xué)調(diào)劑
已經(jīng)有7人回復(fù)
-
一志愿085600中科院寧波所276分求調(diào)劑
已經(jīng)有15人回復(fù)
-
288資源與環(huán)境專碩求調(diào)劑，不限專業(yè)，有學(xué)上就行
已經(jīng)有22人回復(fù)
-
273求調(diào)劑
已經(jīng)有8人回復(fù)
-
267求調(diào)劑
已經(jīng)有9人回復(fù)
-
調(diào)劑推薦
已經(jīng)有8人回復(fù)
-
324分 085600材料與化工
已經(jīng)有8人回復(fù)
-
一志愿 南京航空航天大學(xué) ，080500材料科學(xué)與工程學(xué)碩
已經(jīng)有4人回復(fù)
英語留級生
銅蟲 (小有名氣)
- 應(yīng)助: 1 (幼兒園)
- 金幣: 97.2
- 帖子: 156
- 在線: 9.8小時
- 蟲號: 3388541
- 注冊: 2014-08-29
- 性別: GG
- 專業(yè): 化工系統(tǒng)工程
2樓2014-09-12 10:08:56
cmds1907
鐵桿木蟲 (著名寫手)
- 翻譯EPI: 73
- 應(yīng)助: 72 (初中生)
- 金幣: 10669.3
- 散金: 3999
- 紅花: 17
- 帖子: 2100
- 在線: 530小時
- 蟲號: 3346786
- 注冊: 2014-07-31
- 專業(yè): 有機分子功能材料化學(xué)
【答案】應(yīng)助回帖
★ ★ ★ ★ ★ ★
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-09-12 16:29:56
英語留級生: 金幣+5, 翻譯EPI+1 2014-09-12 21:09:36
RXMCDM: 金幣+1, 多謝應(yīng)助！ 2014-09-12 16:29:56
英語留級生: 金幣+5, 翻譯EPI+1 2014-09-12 21:09:36
|
為了比較自由膨脹條件與約束的條件的影響，在1500°C沒有任何約束下進行了澆注料燃燒5小時的相同測量。針對耐腐蝕性能的測試，使用上述的較高機械強度的相同澆注料，實施了結(jié)構(gòu)限制（約束）。對于這個評價，氧化鋁-CAC澆注料首先如圖2所示成形，固化后(50°C/24h)，經(jīng)過干燥(110°C/24h)和燒結(jié)(1500°C/5h)步驟，鋁鎂澆注料在模內(nèi)孔成形。以600°C/5h預(yù)燃燒（加熱）材料(樣品+約束材料)后，腐蝕試驗在1500°C進行了5個小時，使用10 g的高FeOx鋼包爐渣(表1)。相同的測試條件應(yīng)用于非約束的澆注料(沒有任何氧化鋁- CAC澆注料圍繞在周圍)。 Wayne Rasband 可以譯為 韋恩 拉斯班德 |
3樓2014-09-12 16:10:38
相關(guān)版塊跳轉(zhuǎn)
我要訂閱樓主 英語留級生 的主題更新
| 3 | 1/1 | 返回列表 |
| 最具人氣熱帖推薦 [查看全部] | 作者 | 回/看 | 最后發(fā)表 | |
|---|---|---|---|---|
|
[考研] 267求調(diào)劑 +9 | uiybh 2026-03-31 | 9/450 |
|
|---|---|---|---|---|
|
|
[考研] 一志愿：西北大學(xué)，英一數(shù)一408-284分求調(diào)劑 +7 | 12.27 2026-03-27 | 7/350 |
|
|
[考研] 080200專業(yè)277分，求帶走！ +4 | 瓶子PZ 2026-03-31 | 4/200 |
|
|
|
[考研] 0856材料化工調(diào)劑 總分330 +17 | zhubinhao 2026-03-27 | 17/850 |
|
|
|
[考研] 336材料求調(diào)劑 +10 | 陳瀅瑩 2026-03-26 | 12/600 |
|
|
|
[考研] 308求調(diào)劑 +11 | 墨墨漠 2026-03-25 | 11/550 |
|
|
|
[考研] 343求調(diào)劑 +8 | 愛羈絆 2026-03-28 | 8/400 |
|
|
|
[考研] 本科211安全工程，初試290分，求調(diào)劑 +3 | 2719846834 2026-03-28 | 3/150 |
|
|
|
[考研] 總分322求生物學(xué)/生化與分子/生物信息學(xué)相關(guān)調(diào)劑 +6 | 星沉uu 2026-03-26 | 7/350 |
|
|
|
[考研] 求調(diào)劑 +4 | 研s. 2026-03-25 | 4/200 |
|
|
|
[考研] 一志愿中海洋320化學(xué)工程與技術(shù)學(xué)碩求調(diào)劑 +8 | 披星河 2026-03-30 | 8/400 |
|
|
|
[考研] 哈爾濱工業(yè)大學(xué)材料與化工專碩378求調(diào)劑 +3 | 塔比烏斯 2026-03-30 | 3/150 |
|
|
|
[考研] 296求調(diào)劑 +10 | 彼岸t 2026-03-29 | 10/500 |
|
|
|
[考研] 337求調(diào)劑 +6 | 《樹》 2026-03-29 | 6/300 |
|
|
|
[考研] 070305高分子化學(xué)與物理 304分求調(diào)劑 +12 | c297914 2026-03-28 | 12/600 |
|
|
|
[考研] 0856求調(diào)劑 +13 | zhn03 2026-03-25 | 14/700 |
|
|
|
[考研] 321求調(diào)劑 +7 | 璞玉~~ 2026-03-25 | 8/400 |
|
|
|
[考研] 085701環(huán)境工程，267求調(diào)劑 +16 | minht 2026-03-26 | 16/800 |
|
|
|
[考研] 352分 化工與材料 +5 | 海納百川Ly 2026-03-27 | 5/250 |
|
|
|
[考研] 一志愿鄭大085600，310分求調(diào)劑 +5 | 李瀟可 2026-03-26 | 5/250 |
|